加劲型土工复合材料的制备方法技术
Preparation method of stiffened geosynthetics
The invention is supported by the public welfare special research project (201411006) supported by the Ministry of land and resources. The invention discloses a preparation method of a stiffened type geotechnical composite material, which is characterized in that two layers of non-woven fabric and a layer of PP grid composite sandwich structure, non woven fabrics as the upper PP grid as the core layer, through the needle punching composite reinforcement method, through the test results show that the optimum parameters: needle mill feed line speed is 1.29m/min, the discharge line speed is 1.36m/min, rolling pin specifications for 15x16x 25X 3.5M332G 53017 pin density is 5000 /m, the needle rolling speed is 200needles/min, the depth of needle punching 15mm. This product has good mechanical properties, hydraulic performance and stability, and can be applied to the project that needs stiffening, isolation and protection.
【技术实现步骤摘要】
加劲型土工复合材料的制备方法
本专利技术涉及复合材料应用
，尤其涉及加劲型土工复合材料。
技术介绍
山坡地水土灾害防治工作是一项重要的课题。以工程方法预防灾害或降低对生命财产的伤害是最常见的对策。本专利技术所属
的现有技术如下3点所示，但仍有改善的空间，如专利技术(1)的制品只是单纯的非织物，用于稳定边坡所需的强力恐有不足；专利技术(2)的土工格网无法阻挡土砂的流失，且作为稳定路基及补强底层，不能有效防止相邻的异质土壤或填充料的相互混合；(3)的专利技术使用魔术贴黏合的结合性有待商榷。因此，本专利技术结合非织物与格网，以创造更大的功能性与效益。(1)1997年，台湾，戴华锡专利技术“土工织物之制造方法及其制品”，申请号：086104776。此专利技术是一种土工织物的制造方法及其制品，其是一种将复合纤维材料经气流成网的方式制成适当厚度的垫体，再将该垫体藉针轧及热处理后，即可制成一种内部纤维互相纠结在一起的成品，俾此专利技术所制成的成品使用于山坡上时，厚度不需如传统之土工织物之制造方法及其制品之成品厚，即可抵抗地层所施加的压力，进而稳定山坡之土层，再者，因...
【技术保护点】
一种加劲型土工复合材料的制备方法，其特征在于：使用两层非织物与一层PP格网进行三明治结构的复合，非织物为上下层，PP格网作为芯层，通过针轧加固法进行复合，经由测试结果显示最佳参数：针轧机的入料线速度为1.29m/min，出料线速度为1.36m/min，轧针规格为15x16x25x3.5M332G 53017，植针密度为5000枚/m，针轧速度为200needles/min，针轧深度为15mm。
【技术特征摘要】
1.一种加劲型土工复合材料的制备方法，其特征在于：使用两层非织物与一层PP格网进行三明治结构的复合，非织物为上下层，PP格网作为芯层，通过针轧加固法进行复合，经由测试结果显示最佳参数：针轧机的入料线速度为1.29m/min，出料线速度为1.36m/min，轧针规格为15x16x25x3.5M332G53017，植针密度为5000枚/m，针轧速度为200needles/min，针轧深度为15mm。2.根据权利要求1所...