The present invention relates to a cover glass processing technology field, discloses a molten salt composition and ion exchange strengthened cover glass and toughened by ion exchange method; molten salt composition, with the total weight of the composition as a benchmark, the composition of rare earth oxides containing 80 99.5 wt% KNO3, 0.1 15 wt% K2CO3 and 0.1 5 wt%; toughened glass cover method, including the ion exchange of molten salt composition is heated to the melting, get the melt, the melt in the cover glass will be tempered by ion exchange. According to the method of the invention, the tempering effect can be obviously improved, and the toughened cover glass with high hardness and high bending strength can be obtained.
【技术实现步骤摘要】
离子交换熔盐组合物和钢化盖板玻璃及其钢化方法
本专利技术涉及盖板玻璃强化处理
，具体地，涉及离子交换熔盐组合物和钢化盖板玻璃及其钢化方法。
技术介绍
触摸屏作为一种先进的电子输入设备，具有简单便捷、反应速度快、节省空间和易于人机交流等诸多优点。触摸屏所使用的盖板玻璃厚度均为超薄玻璃，因其具有良好的平整度、光学性能、电绝缘性、耐热稳定性、耐化学性等特性，被广泛应用于电子产品领域。但是盖板玻璃未进行钢化就作为触摸屏使用时，因其存在抗压性差、机械强度低、易碎等缺陷，并不能直接应用于电子器件中，需经过钢化对盖板玻璃表面进行增强，提高盖板玻璃的强度，最终得到钢化盖板玻璃。钢化盖板玻璃具有表面应力大、热稳定性好、钢化后可切割改裁、无变形等优点，对盖板玻璃进行钢化主要是基于离子自然扩散和相互扩散原理：(A+)玻璃+(B+)熔盐＝(B+)玻璃+(A+)熔盐。但是目前市场普遍采用的钢化工艺中容易出现熔盐杂质，影响钢化效果；此外，在使用离子交换方法进行钢化的过程中，离子交换通道堵塞的问题时有发生；而且，常规的钢化盖板玻璃不能兼具高硬度和高抗弯强度，有时因为钢化盖板玻璃过脆甚至出...
【技术保护点】
一种离子交换熔盐组合物，其特征在于，以该组合物的总重量为基准，该组合物含有80‑99.5重量％的KNO3、0.1‑15重量％的K2CO3和0.1‑5重量％的稀土氧化物。
【技术特征摘要】
1.一种离子交换熔盐组合物，其特征在于，以该组合物的总重量为基准，该组合物含有80-99.5重量％的KNO3、0.1-15重量％的K2CO3和0.1-5重量％的稀土氧化物。2.根据权利要求1所述的组合物，其特征在于，以该组合物的总重量为基准，该组合物含有94-99重量％的KNO3、0.5-5重量％的K2CO3和0.2-1重量％的稀土氧化物。3.根据权利要求1或2所述的组合物，其特征在于，所述稀土氧化物为La2O3和/或CeO2，优选地，在所述离子交换熔盐组合物中，K+与稀土氧化物的摩尔比为(94-106):(0.03-3.0)。4.一种盖板玻璃的钢化方法，该方法包括以下步骤：(1)将离子交换熔盐组合物加热至熔化，得到熔液，其中，所述离子交换熔盐组合物为权利要求1-3中任意一项所...
【专利技术属性】
技术研发人员：沈玉国，徐兴军，李俊锋，张广涛，闫冬成，王丽红，郑权，
申请(专利权)人：东旭科技集团有限公司，东旭集团有限公司，
类型：发明
国别省市：北京,11