一种精氨酸稳定的中空泡状硅酸锰纳米粒的制备方法、产品及应用技术
Preparation method, product and application of arginine stabilized hollow bubble manganese silicate nanoparticles
The invention relates to an arginine stable vacuole manganese silicate nanoparticles preparation products and application method, the preparation method comprises the following steps: 1) arginine is dissolved in water, adding cyclohexane mixed and heated, then adding TEOS by the reaction of cyclohexane reaction after complete removal. Get arginine stable silica nanoparticles; silica nanoparticles, 2) will Potassium Permanganate, ethanol and water were mixed hydrothermal reaction, isolated arginine stable vacuole manganese silicate nanoparticles. The prepared arginine stabilized hollow alveolar manganese silicate nanoparticles can produce very good T1 imaging effects during mri.
【技术实现步骤摘要】
一种精氨酸稳定的中空泡状硅酸锰纳米粒的制备方法、产品及应用
本专利技术属于核磁共振成像造影剂制备领域，具体涉及一种精氨酸稳定的中空泡状硅酸锰纳米粒的制备方法、产品及应用。
技术介绍
近年来，核磁共振成像技术(MRI)以其强大的成像能力已经成为临床医学中非常重要的诊断工具。它能够穿透人体的组织深部，实时动态的对疾病损伤和治疗效果进行检测，同时整个检测诊断过程是非侵袭性的，不会给患者带来机体的损伤和痛苦。对于患者机体的异常情况和组织损伤，核磁共振成像技术能够为医生提供准确和详细的诊断依据。因此，核磁共振成像技术在临床诊断中越来越得到患者接受和医生的重视。但是MRI的敏感性和分辨率并不高，因此需在被检测对象中加入一类能改变氢质子弛豫时间的物质来增加核磁共振成像的敏感性和分辨率，这种物质被称为核磁共振造影剂。目前，临床中用到的造影剂多为钆类造影剂，如钆喷葡胺注射液，但是钆作为造影剂对于机体具有潜在的毒性，能够引起肾源性系统性纤维化病变，因此并不能在临床中受到特别的欢迎。近年来，各国的研究机构尝试将合成的氧化铁纳米粒作为T2造影剂，但是T2造影剂是一种阴性对比剂，在成像过程...
【技术保护点】
一种精氨酸稳定的中空泡状硅酸锰纳米粒的制备方法，其特征在于，包括如下步骤：1)将精氨酸溶解于水中，加入环己烷混合后加热，然后再加入正硅酸乙酯进行反应，反应完成后除去环己烷，得到精氨酸稳定的二氧化硅纳米粒；2)将二氧化硅纳米粒、高锰酸钾、乙醇和水混合后进行水热反应，分离得到精氨酸稳定的中空泡状硅酸锰纳米粒。
【技术特征摘要】
1.一种精氨酸稳定的中空泡状硅酸锰纳米粒的制备方法，其特征在于，包括如下步骤：1)将精氨酸溶解于水中，加入环己烷混合后加热，然后再加入正硅酸乙酯进行反应，反应完成后除去环己烷，得到精氨酸稳定的二氧化硅纳米粒；2)将二氧化硅纳米粒、高锰酸钾、乙醇和水混合后进行水热反应，分离得到精氨酸稳定的中空泡状硅酸锰纳米粒。2.根据权利要求1所述的精氨酸稳定的中空泡状硅酸锰纳米粒的制备方法，其特征在于，所述步骤1)中加热至50～60℃。3.根据权利要求1所述的精氨酸稳定的中空泡状硅酸锰纳米粒的制备方法，其特征在于，所述步骤1)中反应时间为20～30h。4.根据权利要求1所述的精氨酸稳定的中空泡状硅酸锰纳米粒的制备方法，其特征在于，所述步骤1)中精氨酸、环己烷与正硅酸...
【专利技术属性】
技术研发人员：凌代舜，李方园，王帅飞，
申请(专利权)人：浙江大学，
类型：发明
国别省市：浙江,33