The invention discloses a two transparent rubber vulcanized outsole and its formula, the formula according to weight calculation, including: br 100, stearic acid 1 3, 40, 30 white carbon black accelerator DM: 1.4 1.5, accelerator TT:0.1 0.3, 9, 2 accelerator H:7 ZnCO3 4, 1.6, 1.4 sulfur transformer oil 13 17, RX 80 resin 5, calcium carbonate 30 3. The bottom of the mixing type butadiene rubber as main material, through mixing, pressed by the mold, transparent rubber vulcanization, high transparency, yellowing resistance from 3 to 4, under the same conditions arkron wear generally below 0.15, can withstand the long time wear, high wear resistance; suitable for use as tennis and other shoes. The wear resistance of high outsole, wide fitness.
【技术实现步骤摘要】
一种二次硫化透明橡胶鞋大底及其配方
本专利技术涉及橡胶
，涉及透明橡胶配方，特别是一种二次硫化透明橡胶鞋大底及其配方。
技术介绍
现有的鞋用透明橡胶大底，通常是用丁苯橡胶为主料制成，这种鞋大底透明度差，透明度小于50％；耐紫外光黄变性能较差，其耐磨性能较差；一般丁苯透明橡胶同等条件下arkron耐磨可以做到0.3以下，只适用于用作篮球鞋及普通鞋大底，并不适用于网球鞋大底及其它对耐磨性能要求较高的鞋大底，适应面较窄。
技术实现思路
本专利技术的目的是针对现有技术的不足，而提供一种二次硫化透明橡胶鞋大底及其配方，这种透明橡胶鞋大底透明度高、耐紫外光黄变性能好和耐磨性能佳，适用于用作网球鞋大底及其它对耐磨性能要求较高的鞋大底，适应面较宽。实现上述目的的技术方案如下：一种二次硫化透明橡胶鞋大底配方，按照重量份计算，包括：顺丁胶100、硬脂酸1-3、白炭黑30-40、促进剂DM1.4-1.5、促进剂TT0.1-0.3、促进剂H7-9、碳酸锌2-4、硫磺1.4-1.6、变压器油13-17、RX-80树脂3-5、碳酸钙30。一种二次硫化透明橡胶鞋大底，采用上述的配方制成。本专利技术的有益效果：采用混炼型顺丁胶为主料经混炼，通过模具压制、硫化制成透明橡胶，透明度高，耐黄变3～4，同等条件下arkron耐磨一般在0.15以下，能经受长时间的磨耗，耐磨性能高；适用于用作网球鞋大底及其它对耐磨性能要求较高的鞋大底，适应面较宽。具体实施方式下面通过实施例对本
技术实现思路
作进一步说明，但不是对本专利技术的限定。实施例：一种二次硫化透明橡胶鞋大底配方，按照重量份计算，包括：顺丁胶1...
【技术保护点】
一种二次硫化透明橡胶鞋大底配方，其特征在于，按照重量份计算，包括：顺丁胶100、硬脂酸1‑3、白炭黑30‑40、促进剂DM 1.4‑1.5、促进剂TT 0.1‑0.3、促进剂H 7‑9、碳酸锌2‑4、硫磺1.4‑1.6、变压器油13‑17、RX‑80树脂 3‑5、碳酸钙 30。
【技术特征摘要】
1.一种二次硫化透明橡胶鞋大底配方，其特征在于，按照重量份计算，包括：顺丁胶100、硬脂酸1-3、白炭黑30-40、促进剂DM1.4-1.5、促进剂TT0.1-0.3、促进剂H7-9、碳酸锌2-4、硫磺1.4-1.6、变压器油13-17、RX-80树脂3-5、碳酸钙30。2.根据权利要求1所述的二次硫化透明橡胶...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。