The present invention discloses a method for manufacturing plaster board without paper. It is a certain mass ratio of gypsum powder, cellulose, modified starch, retarder, water reducing agent as raw material, after mixing into uniform stirring; then mixing mixture evenly into the solution of foaming agent in water, stirring evenly, mixing gypsum slurry evenly; material pump into the molding machine with the pavement, then scrape pulp overflow, the non paper surface gypsum board. No gypsum board is made by the method of the invention, the preparation method is simple, easy to operate, application of a wide range of products, especially the production cost is reduced, eliminating the two layer of paper, no plasterboard forming in the production, pulp is not easy to deviate.
【技术实现步骤摘要】
一种无纸面石膏板的制造方法
本专利技术涉及石膏板生产领域，具体地说是一种高强度无纸面石膏板的制造方法。
技术介绍
石膏板是以建筑石膏为主要原料制成的一种材料。它是一种重量轻、强度较高、厚度较薄、加工方便以及隔音绝热和防火等性能较好的建筑材料，是当前着重发展的新型轻质板材之一。石膏板已广泛用于住宅、办公楼、商店、旅馆和工业厂房等各种建筑物的内隔墙、墙体覆面板(代替墙面抹灰层)、天花板、吸音板、地面基层板和各种装饰板等。目前，在市场上出售很多纸面石膏板，品种规格种类很多，有普通纸面石膏板，有高级普通纸面石膏板，有高级耐火纸面石膏板，有防潮纸面石膏板等等，但这些品种大多为石膏纸面板的两层护面纸，两张护面纸的增加，成本费用也相应增加，粘结不好护面纸，容易脱落，纸张容易跑偏。而目前的公知技术中，尚未很好地克服该技术问题。
技术实现思路
本专利技术的目的是克服现有技术的不足，提供一种无纸面石膏板的制造方法。为达到上述技术目的，本专利技术一种无纸面石膏板的制造方法，是通过以下步骤实现：(1)选取下质量配比的原料：脱硫石膏粉70～100份，石膏纤维1～10份，改性淀粉0.1～10份，...
【技术保护点】
一种无纸面石膏板的制造方法，包括以下步骤：(1)选取下质量配比的原料：脱硫石膏粉70～100份，石膏纤维1～10份，改性淀粉0.1～10份，缓凝剂0.1～5份、减水剂0.1～2份，发泡剂0.2～0.8份；(2)将上述质量配比的脱硫石膏粉、石膏纤维、改性淀粉、缓凝剂、减水剂经过搅拌成均匀的拌和料；(3)再把发泡剂和水加入储浆罐内，储浆罐的温度保持在30～40摄氏度之间，然后把搅拌均匀的拌和料加入储浆罐内进行搅拌，溶有发泡剂的水与拌和料得到混合均匀的石膏料浆；(4)开启泵阀，将料浆泵入带有成型铺装机内，然后刮去溢浆，即得无纸面石膏板。
【技术特征摘要】
1.一种无纸面石膏板的制造方法，包括以下步骤：(1)选取下质量配比的原料：脱硫石膏粉70～100份，石膏纤维1～10份，改性淀粉0.1～10份，缓凝剂0.1～5份、减水剂0.1～2份，发泡剂0.2～0.8份；(2)将上述质量配比的脱硫石膏粉、石膏纤维、改性淀粉、缓凝剂、减水剂经过搅拌成均匀的拌和料；(3)再把发泡剂和水加入储浆罐内，储浆罐的温度保持在30～40摄氏度之间，然后把搅拌均匀的拌和料加入储浆罐内进行搅拌，溶有发泡剂的水与拌和料得到混合均匀的石膏料浆；(4)开启泵阀，将料浆泵入带有成型铺装机内，然后刮去溢浆，即得无纸面石膏板。2.根据权...