一种石膏代木板及其制备方法技术

本发明专利技术公开了一种石膏代木板。它是由高强度石膏、普通石膏粉、石膏纤维、玉米淀粉、柠檬酸为原料制得。将一定配比的高强度石膏粉与普通石膏粉充分混合，再将石膏纤维与玉米淀粉及柠檬酸充分混合，然后再把二者再次充分混合，然后加入水，充分拌和，然后倒入符合使用要求的模型内，加压成型，即得成品。本发明专利技术制备方法简单，易于操作，产品应用广，尤其适用于制做办公用品、家具、易操作，可锯、可刨、可钉、强度高；不加化工添加剂，绿色环保，可彻底规避甲醛对人身体的影响。

Gypsum substitute board and its preparation method

The present invention discloses a gypsum board instead of a board. It is made of high strength gypsum, ordinary gypsum powder, gypsum fiber, corn starch and citric acid as raw materials. The high strength gypsum powder were fully mixed with ordinary gypsum powder, gypsum fiber then fully mixed with starch and citric acid of corn, then put the two again fully mixed, then add water, fully mixing, and then into the meet the requirements of the model, the product is made into compression type. The invention has simple preparation method, easy operation, wide application products, especially suitable for office supplies, furniture, easy to operate, sawing, planing, nailing, high strength; without chemical additives, green environmental protection, can completely avoid the effects of formaldehyde on the human body.

【技术实现步骤摘要】
一种石膏代木板及其制备方法
本专利技术涉及石膏板生产领域，具体地说是一种高性能石膏代木板，本专利技术还涉及该石膏代木板的制备方法。
技术介绍
石膏板是以建筑石膏为主要原料制成的一种材料。它是一种重量轻、强度较高、厚度较薄、加工方便以及隔音绝热和防火等性能较好的建筑材料，是当前着重发展的新型轻质板材之一。石膏板已广泛用于住宅、办公楼、商店、旅馆和工业厂房等各种建筑物的内隔墙、墙体覆面板(代替墙面抹灰层)、天花板、吸音板、地面基层板和各种装饰板等。目前，在市场上出售的板材有很多种类，有石膏板、压缩板、密度板等，随着木质市场的扩大，很多家俱都是实木家俱，实木家俱的价格也很高，在人们要求越来越高的今天，现有的压缩板是使用木屑或其他下脚料加入大量的合成胶水压制而成的，含大量的胶水所以不可避免会有不同程度的污染问题；密度板是以木质纤维或其他植物纤维为原料，施加脲醛树脂或其他适用的胶粘剂制成的板材，并且见水就胀，变形大，握钉力差。上述人造板材，在办公用品、家俱等领域应用时，在人们环保要求越来越高的今天，环保首先放在第一位。综合上述，为了解决现有的板材不加化工原料，可锯、可刨、可钉的要求，而研发了一本文档来自技高网...

【技术保护点】
一种石膏代木板，其特征是由以下质量配备的原料制备得到：高强度石膏20～90份，普通石膏粉1～20份，石膏纤维1～20份，玉米淀粉0.1～1.8份，柠檬酸0.1～1.5份。

【技术特征摘要】
1.一种石膏代木板，其特征是由以下质量配备的原料制备得到：高强度石膏20～90份，普通石膏粉1～20份，石膏纤维1～20份，玉米淀粉0.1～1.8份，柠檬酸0.1～1.5份。2.根据权利要求1所述的石膏代木板，其特征在于所述原料的质量配比为：高强度石膏70份，普通石膏粉15份，石膏纤维15份，玉米淀粉0.85份，柠檬酸0.5份。3....