一种抑制热轧H型钢表面红锈的方法技术
A method of inhibiting red rust on hot rolled H section steel
The invention relates to a method for inhibiting hot-rolled H steel surface red rust, characterized by comprising the following steps: (1) H steel into the rolling mill, at 900 to 1150 DEG C temperature range, avoid roll cooling water in H steel after rolling on the web and flange form the groove to form a residue; (2) after rolling in the output roller and cooling bed, using air cooling, cooling to 100 DEG C; (3) out of bed after cutting H steel at the end, to prevent cutting cooling water into the H type steel web and flange formed by the groove formed residue. This method limits the H type steel high temperature and normal temperature storage, and the interaction of surface water, inhibit the formation of reddish brown FeOOH and Fe2O3, decreased the surface red rust tendency, is conducive to improve the appearance and surface quality.
【技术实现步骤摘要】
一种抑制热轧H型钢表面红锈的方法
本专利技术属于轧钢
，具体涉及一种抑制热轧H型钢表面红锈的方法。
技术介绍
H型钢是一种经济型断面钢材，与普通工字钢相比，由于其形状均匀，力学性能优异，轧制时具备均匀的变形和较小的内应力，故具有截面模数大、重量轻、节省金属，便于拼装等优点，因此广泛用于工业、建筑、桥梁、海洋平台等结构中。传统的H型钢生产，通常经过加热-除鳞-BD1(开坯机breakdown)—BD2—万能轧机—冷床—精整工序，整个热轧过程均在900℃以上，与常规热轧板带材生产相比，H型钢生产线仅在加热炉出口设置除鳞，轧制过程中无除鳞，故轧制期间生成的二次氧化铁皮无法去除，与轧件一同变形，容易压入基体并与之紧密结合，轧后也无表面氧化铁皮处理工序。国内多家H型钢生产企业，都为类似工艺，但均不同程度面临表面红锈问题，而有关H型钢表面红锈控制技术的专利及报道却较少。板带材生产领域有不少针对表面红锈控制措施的报道，如降低成份中的Si含量，提高除鳞温度，增加除鳞压力和道次，防止轧辊辊面脱落等，但针对现有的常规H型钢生产，这些措施或者与工艺冲突，或者根本不具备设备条件。鉴...
【技术保护点】
一种抑制热轧H型钢表面红锈的方法，其特征在于，包括如下步骤：(1)H型钢进入轧机轧制时，在900℃～1150℃轧制温度范围内，避免轧辊冷却水在轧后的H型钢腹板和上翼缘围成的槽内形成残留；(2)终轧后，在输出辊道及冷床上，采用空冷，冷至100℃以下；(3)出冷床后锯切H型钢头尾时，防止锯切冷却水进入H型钢腹板和上翼缘围成的槽内形成残留。
【技术特征摘要】
1.一种抑制热轧H型钢表面红锈的方法，其特征在于，包括如下步骤：(1)H型钢进入轧机轧制时，在900℃～1150℃轧制温度范围内，避免轧辊冷却水在轧后的H型钢腹板和上翼缘围成的槽内形成残留；(2)终轧后，在输出辊道及冷床上，采用空冷，冷至100℃以下；(3)出冷床后锯切H型钢头尾时，防止锯切冷却水进入H型钢腹板和上翼缘围成的槽内形成残留。2.根据权利要求1所述一种抑制热轧H型钢表面红锈的方法...
【专利技术属性】
技术研发人员：韩会全，王万慧，
申请(专利权)人：中冶赛迪技术研究中心有限公司，
类型：发明
国别省市：重庆,50