The present invention aims to provide a crosslinkable thermoplastic low permeability oil elastomer material. The material is composed of 40 ~ 60, 40 ~ 60 POE resin silane grafted POE and from 40 to 80, 5 to 15 portions of polyvinyl alcohol fiber POE MAH. The advantages of the material is also has good oil resistance, low permeability, high strength, low creep, low density, easy processing, low manufacturing cost and the rate of oil, raw fiber material the use of non-toxic, non irritating to the human body and natural degradation, safety and environmental protection. The products formed by the material of the invention can be adjusted to a certain temperature and humidity to produce oil resistant products with crosslinking structure, which is suitable for the manufacture of oil contact parts such as oil pipe fittings and oil seals.
【技术实现步骤摘要】
一种可交联的热塑性低渗油弹性体材料
本专利技术属于高分子复合材料
，涉及一种可交联的热塑性低渗油弹性体材料。
技术介绍
低渗油弹性体材料主要应用于油管、油封等油路密封结构，需具备耐油、低渗透等特性，现有技术通常采用聚四氟乙烯、硅橡胶、氟橡胶等材料制备。以上材料价格昂贵，且熔体粘度极大，只能采用模压、烧结等低效成型方式成型，成型时间长，工艺费用高。同时以上材料废弃物处理会产生有毒有害气体，环境危害较大。采用热塑性弹性体制备油封材料具有高效成型的优势，但耐油性较差，渗油率高。所以，研制可快速成型、环境友好型的低渗油弹性体材料十分必要。
技术实现思路
本专利技术的目的在于提供一种可交联的热塑性低渗油弹性体材料。本专利技术采用POE树脂为基体，添加聚乙烯醇纤维和硅烷接枝聚合物，经分散和增容后，聚乙烯醇纤维以网状结构分散于基体树脂中。该材料可采用注射或挤出等高效成型方式成型。成型后的制品在一定温湿度环境下调节，即可生成具有一定交联度的低渗油制品，具备耐油性好，渗油率低，回弹性好等特点。本专利技术通过下述方案实现技术目标：可交联的热塑性低渗油弹性体材料，由40～60份POE...
【技术保护点】
一种可交联的热塑性低渗油弹性体材料，由40～60份POE树脂、40～60份硅烷接枝POE、40～80份聚乙烯醇纤维、5～15份POE‑MAH组成。
【技术特征摘要】
1.一种可交联的热塑性低渗油弹性体材料，由40～60份POE树脂、40～60份硅烷接枝POE、40～80份聚乙烯醇纤维、5～15份POE-MAH组成。2.根据权利要求1所述的一种可交联的热塑性低渗油弹性体材料，其特征在于，所述POE树脂为乙烯-辛烯共聚物，其熔融温度不高于90℃。3.根据权利要求1所述的一种可交联的热塑性低渗油弹性体材料，其特征在于，所述硅烷接枝POE，其熔融温度不高于90℃，硅烷接枝含量为2％～3％。4.根据权利要求1所述的一种可交联的热塑性低渗油弹性体材料，其特征在于，所述聚乙烯醇纤维，其水中...
【专利技术属性】
技术研发人员：翟道兴，
申请(专利权)人：余姚市顺迪塑料模具厂，
类型：发明
国别省市：浙江,33