一种纳米纤维素的制备方法技术
Preparation method of nano cellulose
The present invention relates to the field of nano cellulose, and discloses a method for preparing nano cellulose, the method comprises the following steps: (1) the pulp dispersion and hydrogen peroxide contact reaction, the product of the contact reaction after solid-liquid separation; (2) in the TEMPO oxidation conditions, solid phase and TEMPO the solid-liquid separation of income the oxidation reaction. The method of the invention can be prepared in high yield high purity nano cellulose, and the corrosion reaction system of the method of small, low requirement on equipment, the reaction is convenient and easy, mild reaction conditions, very suitable for industrial production of nano cellulose.
【技术实现步骤摘要】
一种纳米纤维素的制备方法
本专利技术涉及纳米纤维素领域，具体地，涉及一种纳米纤维素的制备方法。
技术介绍
纳米纤维素(cellulosenanofiber，CNF)是一种直径为纳米尺度(1～100nm)而长度较大的具有一定长径比的线状纳米材料。与普通纤维素相比，纳米纤维素因其纳米效应而具有较大表面积(普通微米纤维素的1000倍)、高结晶度、高杨氏模量、高强度、超精细结构及高透明度等特性，可应用于造纸、气凝胶、隐身衣、生物组织工程、柔性及可穿戴电子等产业中。再加之具有生物材料的轻质、可再生、可降解及生物相容性等优异性能，使其在高性能复合材料中具有广阔的应用前景。纳米纤维素的制备方法主要有化学法、生物法及物理法。每种方法都有一定的局限，化学法需要用强酸水解，对反应设备要求高，回收和处理后续残留物困难；生物法制备细菌纤维素复杂、耗时长、成本高、价格贵；物理法制备纳米纤维素需要采用特殊的设备或使用高压，能量消耗比较高，所得物纯度低，影响使用效果。因此，进一步研究改良纳米纤维素生产方法至关重要。
技术实现思路
本专利技术的目的在于克服现有的制备纳米纤维素的方法存在的设备要求高、...
【技术保护点】
一种纳米纤维素的制备方法，其特征在于，该方法包括：(1)将纸浆分散液与过氧化氢进行接触反应，将该接触反应后的产物进行固液分离；(2)在TEMPO氧化条件下，将所述固液分离所得的固相与TEMPO进行氧化反应。
【技术特征摘要】
1.一种纳米纤维素的制备方法，其特征在于，该方法包括：(1)将纸浆分散液与过氧化氢进行接触反应，将该接触反应后的产物进行固液分离；(2)在TEMPO氧化条件下，将所述固液分离所得的固相与TEMPO进行氧化反应。2.根据权利要求1所述的方法，其中，相对于100重量份的以干重计的所述纸浆分散液，过氧化氢的用量为10-200重量份，优选为20-150重量份；优选地，所述纸浆分散液的浓度为15-25重量％。3.根据权利要求2所述的方法，其中，所述过氧化氢以过氧化氢溶液的形式提供，且该过氧化氢溶液的pH值为9-12；优选地，所述过氧化氢溶液的浓度为1-10重量％，更优选为2-5重量％。4.根据权利要求1-3中任意一项所述的方法，其中，所述接触反应的条件包括：温度为30-70℃，时间为1-10h。5.根据权利要求1所述的方法，其中，相对于100重量份的所述固液分离所得的固相，TEMPO的用量为0.5-5重量份；优选地，所述固液分离所得的固相以其在水中的分散液...
【专利技术属性】
技术研发人员：智云霞，高鹏辉，赵珍，黄宏伟，
申请(专利权)人：新材料与产业技术北京研究院，
类型：发明
国别省市：北京,11