The present invention discloses a filling slurry for doping waste concrete aggregate in coal mine. The filling slurry is composed of the following percentage of raw materials: 8 - 12% cement, 18 - 22% fly ash, 24 - 28% coal gangue, 22 - 26% waste concrete aggregate, and residual water. The present invention has developed a slurry for replacing coal gangue with waste concrete coarse and fine aggregate, which can meet the requirements of fluidity and strength of coal mine filling. Due to the large amount of coarse and fine aggregate of municipal waste concrete, it provides a good solution for the treatment of urban concrete construction waste, which is conducive to the protection of the environment. In addition, because of the strength of slurry is higher than the existing coal gangue, it can further strengthen the safety of the mine.
【技术实现步骤摘要】
一种煤矿用掺杂废弃混凝土骨料的充填料浆
本专利技术涉及一种煤矿用掺杂废弃混凝土骨料的充填料浆。
技术介绍
膏体充填技术是1979年德国在格伦德铅锌矿首先发展起来的，由于膏体充填具有料浆浓度高、充填效率高、成本较低，这项技术试验成功以后在金属矿山得到较快的发展，在包括我国在内的许多国家得到应用。固体废物膏体充填不迁村采煤，就是把煤矿附近的煤矸石、粉煤灰等在地面加工制作成不需要脱水处理的牙膏状浆体，采用充填泵或重力加压，通过管道输送到井下，适时充填采空区或离层区，形成以膏体充填体为主的上覆岩层支撑体系，有效控制地表沉陷在建筑物允许值范围内，实现村庄不搬迁，安全开采建筑物下压煤，保护矿区生态环境和地下水资源。但矸石、粉煤灰等固体废弃物在再生利用上已取得了新进展，导致充填开采原材料在数量上难以满足需求，制约了充填开采技术的全面实施。所以，亟需寻找新的替代原料。另一方面，随着我国经济建设的快速发展，每年会产生数亿吨的建筑垃圾，其中废弃混凝土约占41％，大多堆放于城市周边，既占用土地资源又污染周围环境。因此，若能将废弃混凝土用于制备充填材料，既可解决充填原材料不足的问题，又可...
【技术保护点】
一种煤矿用掺杂废弃混凝土骨料的充填料浆，其特征在于：由以下质量百分比的原料组成：8～12％水泥，18～22％粉煤灰，24～28％煤矸石、22～26％废弃混凝土骨料，余量为水。
【技术特征摘要】
1.一种煤矿用掺杂废弃混凝土骨料的充填料浆，其特征在于：由以下质量百分比的原料组成：8～12％水泥，18～22％粉煤灰，24～28％煤矸石、22～26％废弃混凝土骨料，余量为水。2.根据权利要求1所述的一种煤矿用掺杂废弃混凝土骨料的充填料浆，其特征在于：水泥为32.5、32.5R、42.5、42.5R型水泥的至少一种。3.根据权利要求1所述的一种煤矿用掺杂废弃混凝土骨料的充填料浆，其特征在于：粉煤灰为Ι级或Ⅱ级F类粉煤灰中的至少一种。4.根据权利要求1所述的一种煤矿用掺杂废弃混凝土骨料的充填料浆，其特征在于：煤矸石为粒径<5mm的细煤矸石和粒径为5mm～15mm的粗煤矸石...
【专利技术属性】
技术研发人员：陈锡麟，陈忠平，李鹏，潘敏尧，何威，冯波宇，伍航宇，黄小波，黄威龙，张善硕，赵泽民，
申请(专利权)人：固岩科技发展有限公司，
类型：发明
国别省市：广东,44
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。