一种导电胶及制备方法技术

本发明专利技术提供了一种导电胶及制备方法，所述导电胶包括如下组分：改性环氧树脂、酚醛树脂、镀银铜粉、石墨、稀释剂、消泡剂、固化剂、促进剂。制备方法包括：首先将改性环氧树脂、酚醛树脂混合搅拌均匀，然后再依次加入剩余组分，充分反应混合均匀后；将其置于半自动液体灌装机中，由灌装机装到胶管中，即制得导电胶。本发明专利技术所述导电胶具有较好的粘结牢固性、耐热性能和优异的导电性能，具有较好的使用价值。

Conductive adhesive and preparation method thereof

The conductive adhesive comprises the following components: modified epoxy resin, phenolic resin, silver plated copper powder, graphite, diluent, defoaming agent, curing agent and accelerator. The preparation method comprises: firstly, modified epoxy resin, phenolic resin and mixed evenly, then add the remaining ingredients, full reaction after mixing; the semi automatic liquid filling machine, filling machine is fitted to the hose, is made of conductive adhesive. The invention of the conductive adhesive has a good adhesive fastness, heat resistance and excellent electrical properties, has good use value.

【技术实现步骤摘要】
一种导电胶及制备方法
本专利技术涉及电力工具
，具体地，涉及一种导电胶及制备方法。
技术介绍
导电胶是一种固化或干燥后具有一定导电性能的胶黏剂，它通常以基体树脂和导电填料即导电粒子为主要组成成分，通过基体树脂的粘接作用把导电粒子结合在一起，形成导电通路，实现被粘材料的导电连接。由于导电胶的基体树脂是一种胶黏剂，可以选择适宜的固化温度进行粘接，同时，由于电子元件的小型化、微型化及印刷电路板的高密度化和高度集成化的迅速发展，而导电胶可以制成浆料，实现很高的线分辨率。而且导电胶工艺简单，易于操作，可提高生产效率，所以导电胶是替代铅锡焊接，实现导电连接的理想选择。现有的导电胶普遍存在耐热性能差，电导率低的缺点，使用要求较高的情况下并不能满足要求。
技术实现思路
针对现有技术中的缺陷，本专利技术的目的是提供一种导电胶及制备方法，所述导电胶具有较好的粘结牢固性、耐热性能和优异的导电性能，具有较好的使用价值。本专利技术解决技术问题采用如下技术方案：本专利技术涉及一种导电胶，包括如下重量份的各组分：改性环氧树脂30~46份、酚醛树脂15~28份、镀银铜粉5~10份、石墨3~6份、稀释剂4~9份、消本文档来自技高网...

【技术保护点】
一种导电胶，其特征在于，包括如下重量份的各组分：改性环氧树脂30~46份、酚醛树脂15~28份、镀银铜粉5~10份、石墨3~6份、稀释剂4~9份、消泡剂3~7份、固化剂2~5份、促进剂1~3份。

【技术特征摘要】
1.一种导电胶，其特征在于，包括如下重量份的各组分：改性环氧树脂30~46份、酚醛树脂15~28份、镀银铜粉5~10份、石墨3~6份、稀释剂4~9份、消泡剂3~7份、固化剂2~5份、促进剂1~3份。2.根据权利要求1所述的导电胶，其特征在于，所述改性环氧树脂38份、酚醛树脂22份、镀银铜粉8份、石墨5份、稀释剂6份、消泡剂5份、固化剂3份、促进剂2.5份。3.根据权利要求1所述的导电胶，其特征在于，所述改性环氧树脂为有机硅改性环氧树脂、有机钛改性环氧树脂、石墨烯改性环氧树脂中的任一种。4.根据权利要求1所述的导电胶，其特征在于，所述稀释剂为甲苯、邻苯二甲酸二辛酯、丁二醇二缩水甘油醚中的任一种。5.根据权利要求1所述的导电胶，其特征在于，所述固化剂为二甲基苯胺、甲基四氢苯酐、十二烷基顺丁烯二酸酐中的任一种。6.根据权利要求1所...

【专利技术属性】
技术研发人员：孔令翠，
申请(专利权)人：合肥欧仕嘉机电设备有限公司，
类型：发明
国别省市：安徽,34