The invention discloses a water resistant epoxy resin adhesive for decorative sheet, with weight, including bisphenol S type epoxy resin base material 320 500 copies, twelve ene sueeinie anhydride curing agent 52 83 copies, two DMF and 18 32 copies, 42 copies of packing 28 liquid polysulfide rubber. 19 gum 27, methyl phosphonic acid methyl 32 17 two. The reasonable control of the ratio of reactants, reaction conditions and reasonable control of preparation of a kind of application to high durability of epoxy resin adhesive in light industry and textile industry, has good moisture resistance, excellent heat resistance, excellent performance and impact resistance and other mechanical properties, good adhesion performance, durability well, the preparation method is simple and feasible, suitable for industrialized production.
【技术实现步骤摘要】
一种用于装饰板材粘接的耐水环氧树脂
本专利技术涉及高分子凝胶领域，具体是指一种用于装饰板材粘接的耐水环氧树脂。
技术介绍
房屋装修粘合剂作为轻工业行业常用的粘合产品广泛的应用于装饰塑料或木质材料加工等领域，对于房屋装修来说，在粘接多层材料时需要用到粘接剂。而目前常用的普通粘接剂通常含有醛类等有机毒物，其释放会影响人体健康。所以，如何解决普通粘接剂释放污染气体是亟需解决的技术问题。而环氧树脂胶粘剂作为一种环保型凝胶材料能够解决现有建筑粘合剂的问题，所述的环氧树脂胶粘剂是一类由环氧树脂基料、固化剂、稀释剂、促进剂和填料配制而成的工程胶粘剂。由于其粘接性能好、功能性好、价格比较低廉、粘接工艺简便，所以近几十年来在家电、汽车、水利交通、电子电器和宇航工业领域得到了广泛的应用。随着高新技术和纳米技术的不断发展，近年来，对环氧树脂的改性不断深入，互穿网络、化学共聚和纳米粒子增韧等方法广泛应用，由环氧树脂配制成的各种高性能胶粘剂品种也越来越多。但是它有一个明显的缺点即固化后韧性不足、耐冲击性差、容易开裂，该缺点大大限制了环氧树脂的应用。各种材料的飞速发展对环氧树脂的特性要求越来...
【技术保护点】
一种用于装饰板材粘接的耐水环氧树脂，其特征在于：以重量份表示，包括双酚S型环氧树脂基料320‑500份，十二烯基琥珀酸酐固化剂52‑83份，二甲基甲酰胺18‑32份，填料28‑42份，液体聚硫橡胶19‑27份，甲基膦酸二甲酯17‑32份。
【技术特征摘要】
1.一种用于装饰板材粘接的耐水环氧树脂，其特征在于：以重量份表示，包括双酚S型环氧树脂基料320-500份，十二烯基琥珀酸酐固化剂52-83份，二甲基甲酰胺18-32份，填料28-42份，液体聚硫橡胶19-27份，甲基膦酸二甲酯17-32份。2.根据权利要求1所述的一种用于装饰板材粘接的耐水环氧树脂，其特征在于：所述填料为石墨微粉。3.根据权利要求1所述的一种用于装饰板材粘接的耐水环氧树脂，其特征在于：所述双酚S型环氧树脂基料330份，十二烯基琥珀酸酐固化剂54份，二甲基甲酰胺...
【专利技术属性】
技术研发人员：何金蓉，
申请(专利权)人：成都杰雷遮阳工程有限公司，
类型：发明
国别省市：四川,51
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。