The invention discloses a hydrophobically associating polymer shear recovery performance testing methods, including: (a) first, the preparation of hydrophobically associating polymer (b); then, the hydrophobically associating polymer by solvent dissolved into solution; (c) the hydrophobically associating polymer solution on the vessel; (d) the container respectively. In a water bath; (E) shear environment with certain speed of hydrophobically associating polymer solution of the next period of time, and stop shear, the viscometer measured the apparent viscosity of hydrophobically associating polymer in different restoration time under the table, through the analysis of the data, so that the hydrophobic associating polymer shear recovery performance. The invention can successfully test the shearing recovery property of the hydrophobically associating polymer, and the test result is accurate, the testing step is simple, and the testing cost is greatly reduced.
【技术实现步骤摘要】
本专利技术涉及一种疏水缔合聚合物剪切恢复性能的测试方法。
技术介绍
疏水缔合聚合物，是指聚合物亲水性大分子链上带有少量疏水基团的水溶性聚合物。在水溶性大分子链上引入少量的疏水基团使其水溶液表现出独特的流变性能。在一定的聚合物浓度之上，疏水部分缔合形成动态的三维网络结构，从而形成很大的超分子链聚集体，增大聚合物的流体力学体积，显著地提高溶液的粘度。小分子电解质的加入可增加溶剂的极性，使疏水缔合作用增强，产生明显的抗氯化钙性。在高剪切作用下，疏水缔合形成的动态物理交联网络结构被破坏，溶液粘度下降，剪切作用降低或消除后大分子链间的物理交联重新形成，粘度又将恢复，不发生一般高分子量的聚合物在高剪切速率下的不可逆机械降解。正是由于其独特的溶液性质，它可能在许多领域得到应用，如三次采油、制药、太阳能转换、化妆品、涂料、水处理及减阻剂等。近年来其相关研究倍受关注。疏水亲酯现象是很普遍的，在临界缔合浓度以下，主要形成分子内缔合，其结果是使线团收缩，流体力学体积减小；在CAC以上则主要形成以分子间缔合为主的超分子结构而具有较好的增粘性。通过分子间缔...
【技术保护点】
疏水缔合聚合物剪切恢复性能的测试方法，其特征在于，包括以下步骤：（a）首先，制备疏水缔合聚合物；（b）然后，将疏水缔合聚合物通过溶剂溶解成溶液；（c）取疏水缔合聚合物溶液置于实验容器中；（d）将实验容器分别置于水浴中；（e）对疏水缔合聚合物溶液施以一定速度的剪切环境下剪切一段时间，停止剪切后，通过粘度计测得不同恢复时间下的疏水缔合聚合物的表观粘度，通过分析数据，从而得出疏水缔合聚合物剪切恢复性能。
【技术特征摘要】
1.疏水缔合聚合物剪切恢复性能的测试方法，其特征在于，包括以下步骤：
（a）首先，制备疏水缔合聚合物；
（b）然后，将疏水缔合聚合物通过溶剂溶解成溶液；
（c）取疏水缔合聚合物溶液置于实验容器中；
（d）将实验容器分别置于水浴中；
（e）对疏水缔合聚合物溶液施以一定速度的剪切环境下剪切一段时间，停止剪切后，通过粘度计测得不同恢复时间下的疏水缔合聚合物的表观粘度，通过分析数据，从而得出疏水缔合聚合物剪切恢复性能。
2.根据权利要求1所述的疏水缔合聚合物剪切恢复性能的测试方法，其特征在于，所述实验容器为烧杯。
3.根据权利要求1所述的疏水缔合聚合物剪切恢...