The synthesis process of the invention discloses a LiBOB preparation of two fluorine lithium oxalate borate, comprises the following steps: the LiBOB with fluorine, boron, lithium compound, at 0 to 150 DEG C, reaction pressure on the 101kpa to the reaction system between 150kPa and solvent systems in reaction products at a certain temperature after crystallization vacuum drying to obtain battery grade two fluorine lithium oxalate borate. The invention has novel process and mild condition, and can obtain high-purity battery two, oxalic acid, boric acid and lithium salt.
【技术实现步骤摘要】
一种用双草酸硼酸锂制备二氟草酸硼酸锂的合成工艺
本专利技术涉及锂离子电池行业所用的电解质锂盐的合成工艺，具体涉及到二氟草酸硼酸锂的合成工艺。技术背景电解质盐是锂离子电池的重要组成部分，它的研究开发对锂离子二次电池的性能和发展非常重要。目前，常用锂离子电池的电解质主要为六氟磷酸锂(LiPF6)、双草酸硼酸锂(LiBOB)、四氟硼酸锂(LiBF4)等。LiPF6的热稳定性较差，易潮解，且必须配合碳酸乙烯酯(EC)使用，才能在碳负极表面形成稳定的固体电解质界面(SEI)膜；而EC的熔点为37℃，会对低温性能造成影响。LiBF4作为锂盐的电荷传递电阻较低，使电池具有相对使用LiPF6时更好的低温性能，但对水不稳定，且难以在负极表面形成SEI膜，使组装电池的循环性能较差。二氟草酸硼酸锂(lithiumoxalyldifluoroborate)(亦称LiODFB,LiDFOB,LiFOB)由美国学者ShengShuiZhang首先提出的，CASNo：409071-16-5、化学式LiBC2O4F2，分子量143.77g/mol，分解温度240℃，参见Anuniquelit...
【技术保护点】
一种用双草酸硼酸锂制备二氟草酸硼酸锂的合成工艺，其特征在于，所述工艺包括以下操作步骤：1)、将双草酸硼酸锂与含氟、硼、锂的化合物按比例混合，得到混合物；2)、将步骤1)中的混合物加入到溶媒中，在0～150℃下，反应压力在101kpa‑150kpa下，反应得到产物，将产物经结晶、真空干燥得到二氟草酸硼酸锂。
【技术特征摘要】
1.一种用双草酸硼酸锂制备二氟草酸硼酸锂的合成工艺，其特征在于，所述工艺包括以下操作步骤：1)、将双草酸硼酸锂与含氟、硼、锂的化合物按比例混合，得到混合物；2)、将步骤1)中的混合物加入到溶媒中，在0～150℃下，反应压力在101kpa-150kpa下，反应得到产物，将产物经结晶、真空干燥得到二氟草酸硼酸锂。2.如权利要求1所述的合成工艺，其特征在于，所述含氟、硼、锂的化合物为四氟硼酸锂、氟硼酸、三氟化硼碳酸二甲酯络合物、氟化锂、三氟化硼、三氟化硼乙腈、三氟化硼乙醚，三氟化硼碳酸二甲酯、三氟化硼乙酸乙酯、三氟化硼四氢呋喃、三氟化硼甲醚络合物、三氧化二硼、硼砂、硼酸、碳酸锂、草酸锂、氯化锂、草酸氢锂、氢氧化锂、硫酸锂、磷酸二氢锂、氟化锂、氧化锂、溴化锂、氨基锂、二异丙基氨基锂中的任意一种或者组合。3.如权利要求1所述的合成工艺，其特征在于，所述含氟、硼、锂的化合物为四氟硼酸锂、氟硼酸、氟化锂、三氟化硼、三氟化硼乙腈、三氟化硼乙醚，三氟化硼碳酸二甲酯、三氟化硼乙酸乙酯、三氟化硼四氢呋喃、硼砂、硼酸、碳酸锂、草酸锂、氯化锂、草酸氢锂、氢氧化锂、硫酸锂、三氟化硼碳酸二甲酯络合物、磷酸二氢锂、氟化锂、氧化锂、溴化锂、氨基锂中的任意一种或者组合。4.如权利要求1所述的合成工艺，其特征在于，所...
【专利技术属性】
技术研发人员：杨焜，
申请(专利权)人：上海如鲲新材料有限公司，
类型：发明
国别省市：上海,31