一种铝纳米颗粒及其制备方法技术
Aluminium nano particle and preparation method thereof
The invention relates to an aluminum nanometer particle and a preparation method thereof, belonging to the field of inorganic advanced nano material technology. Aluminum nanoparticles, with a diameter of 15~1000 nm. Preparation method: aluminum source added to the organic ammonium salt in the reaction solution, heating solution; adding lithium aluminum hydride into the solution, and the obtained mixture at 100 to 165 DEG C temperature 1 ~ 72 hours, to obtain the aluminum nano particle suspension; solid-liquid separation, the solid as the aluminum nanoparticles. The preparation method of aluminum nanoparticles is simple and effective solvothermal method, so that the prepared aluminum nanoparticles have high particle content and little impurities.
【技术实现步骤摘要】
一种铝纳米颗粒及其制备方法
本专利技术属于无机先进纳米材料
，具体涉及一种铝纳米颗粒及其制备方法。
技术介绍
铝纳米粒子是指晶粒尺寸为纳米级的超细铝材料。与传统的含能材料相比，铝纳米粒子由于能量密度大、耗氧量低及高的反应活性而成为火箭推进剂和火炸药配方独特的成分之一。纳米铝与其他金属氧化物纳米材料自组装后还可以提高燃烧速度增强冲击波，可望将靶向药物输送到癌细胞，同时不损伤健康细胞。此外，近年来贵金属纳米粒子的制备与应用已经较为成熟，但是由于贵金属成本较高，制约了金属纳米材料的大规模应用，相比之下铝作为地壳中含量最高的金属，具有成本低，易得到等优点，是良好的金属纳米材料，有望实现大规模的应用。随着现在太阳能电池的材料以及制作水准的不断提高，太阳能电池的少子寿命也不断增加，从现在商业太阳电池来看，为了降低太阳能电池的成本提高效率，生产厂家也在不断减少硅片厚度以降低原材料价格，因此为了提高电池的效率，必须考虑降低电池背表面的复合速度，提高长波光谱响应，所以铝背场的好坏将直接影响到太阳能电池的输出特性，颗粒尺寸越小，铝浆与硅片接触越好，此外铝颗粒越小，熔点越低，越易...
【技术保护点】
一种铝纳米颗粒，其特征在于，为纯净的铝纳米颗粒，其直径为15～1000纳米。
【技术特征摘要】
1.一种铝纳米颗粒，其特征在于，为纯净的铝纳米颗粒，其直径为15～1000纳米。2.按照权利要求1所述的铝纳米颗粒，其特征在于，面心立方(fcc)晶型的金属铝。3.制备权利要求1所述的铝纳米颗粒的方法，其特征在于，包括以下步骤：(1)配制铵盐的有机溶液：将铵盐加入有机溶液中，配制成含有铵盐的有机反应液；(2)引入铝盐：将铝源加入到上述铵盐的有机反应液中，升温使其充分溶解；(3)引入还原剂：将氢化铝锂加入到上述溶液中，然后将得到的混合物在100℃～165℃的温度下反应1～72小时，得到铝纳米颗粒悬浮液；(4)对上述铝纳米颗粒悬浮液进行固液分离，所得固体即为所述铝纳米颗粒。4.根据权利要求3所述的方法，其特征在于，步骤(4)所述的固液分离包括以下步骤：先离心浓缩、再超声洗涤，最后真空干燥，其中超声洗涤过程所使用的洗涤液为丙酮、冰甲醇、乙醚之一或它们的混合物。5.根据权利要求3所述的方法，其特征在于，步骤(...
【专利技术属性】
技术研发人员：罗亮，李杨，刘英兰，
申请(专利权)人：北京化工大学，
类型：发明
国别省市：北京,11