The present invention provides a conductive ceramic coating and use method thereof, the technical main points that comprises the following raw materials in parts by weight: 60 silver resin 5 98 copies, 15 copies, 2 copies of 0.5 Ti, SC 1 2.5 copies, 1 copies of 0.1 tin, zirconium 0.1 1 copies, 0.1 lawrencium 0.4, PT 0.1 0.5 copies, 1 copies of 0.1 antioxidants, the magnetic conductive agent 0.1 1. When the utility model is used, the raw material with the same weight is mixed and evenly coated on the ceramic container, and then the product is finished after being fired from 650 degrees Celsius to 800 degrees celsius. The ceramic utensils coated with the invention can not only have decorative effect, but also have the special functions of conducting magnetism and conducting magnetism.
【技术实现步骤摘要】
本专利技术涉及一种陶瓷涂料,具体涉及一种陶瓷导电涂料及其使用方法。
技术介绍
现有陶瓷导电涂料的导磁导电抗氧化时间短,而且要把银用其它涂料封闭以使快速氧化掉的白银不至于被看到,且现有陶瓷导电涂料是膏状,不好进行施工应用,其操作繁琐、费时费力。
技术实现思路
本专利技术提供了一种陶瓷导电涂料及其使用方法,使用本涂料涂布烧制的陶瓷器具不仅具有装饰效果,同时还具有优良的导电导磁性能。本专利技术的陶瓷导电涂料,为实现上述目的所采用的技术方案在于包括以下重量份数的原料:白银60-98份树脂5-15份钛0.5-2份钪1-2.5份锡0.1-1份锆0.1-1份铹0.1-0.4份铂0.1-0.5份抗氧化剂0.1-1份导磁导电剂0.1-1份。作为本专利技术的进一步改进,白银80-90份树脂6-12份钛0.8-1.5份钪1.3-1.8份锡0.3-0.8份锆0.3-0.8份铹0.原有的产品只是膏状不好施工应用,本专利技术有配制相应的助剂可以无限度调整粘度适应各种施工涂布要求,包括各种印刷。15-0.3份铂0.2-0.4份抗氧化剂0.3-0.7份导磁导电剂0.3-0.7份。作为本专利技术的进一步改进,白银86份树脂9份钛1.0份钪1.5份锡0.5份锆0.5份铹0.2份铂0.3份抗氧化剂0.5份导磁导电剂0.5份。作为本专利技术的进一步改进,所述白银为99.999%纯度白银。作为本专利技术的进一步改进,所述导磁导电剂铹铂加工成的液体。上述陶瓷导电涂料的使用方法为:均匀地将陶瓷导电涂料涂布在陶瓷容器上,进行650摄氏度至800摄氏度烧制后即得成品。本专利技术的有益效果是:将本专利技术的涂 ...
【技术保护点】
一种陶瓷导电涂料,其特征在于包括以下重量份数的原料:白银60‑98份 树脂5‑15份 钛0.5‑2份 钪1‑2.5份锡0.1‑1份 锆0.1‑1 份 铹0.1‑0.4份 铂0.1‑0.5份抗氧化剂0.1‑1份 导磁导电剂0.1‑1份。
【技术特征摘要】
1.一种陶瓷导电涂料,其特征在于包括以下重量份数的原料:白银60-98份树脂5-15份钛0.5-2份钪1-2.5份锡0.1-1份锆0.1-1份铹0.1-0.4份铂0.1-0.5份抗氧化剂0.1-1份导磁导电剂0.1-1份。2.如权利要求1所述的一种陶瓷导电涂料,其特征在于:白银80-90份树脂6-12份钛0.8-1.5份钪1.3-1.8份锡0.3-0.8份锆0.3-0.8份铹0.15-0.3份铂0.2-0.4份抗氧化剂0.3-0.7份导磁导电剂0.3-0.7份。3.如权利...