A method for producing flame retardant, relates to a production method of chemical products, POCl3 and catalyst mixed anaerobic conditions after heating to 40 to 60 DEG C, the insulation conditions adding epoxy ethane or propylene oxide and epichlorohydrin, then slowly heating up to 80 DEG C to 60 ~ 3 hours old. After aging liquid test acid value is less than or equal to 0.2mgKOH/g, the material, namely phosphorus flame retardant. The method of the invention has the advantages of simple manufacturing process, effectively improved a lot of phosphorus caused to the crude product washing needs in the original production method cannot deal with the problem of wastewater, sewage pollution; without water washing can get low acid value, and can get a higher flash point, and the good heat storage stability; catalyst the preparation is simple, no air pollution; suitable for industrial use.
【技术实现步骤摘要】
本专利技术涉及一种化工产品的生产方法，具体涉及磷系阻燃剂的生产方法。
技术介绍
随着社会经济的发展，电子电器材料、汽车、高层建筑、交通运输（高速铁路、飞机）等领域由于防火安全的需要，所使用的材料强制需要阻燃，以便减少火灾的发生和保护人民生命财产安全，而阻燃剂中最常见的莫过于TCEP、TCPP以及TDCP，其三者都为添加型阻燃剂，使用方便，价格便宜，具有很大的市场竞争力。三（2-氯乙基）磷酸酯，简称TCEP。在聚氨酯软泡、硬泡生产中都能使用，其具有改善耐水性、耐寒性、抗静电性、手感柔软等作用。一般TCEP由三氯氧磷和环氧乙烷按一定的比例反应所得。三（2-氯丙基）磷酸酯，简称TCPP。主要用于聚氨酯泡沫塑料的阻燃剂，同时也用于聚氯乙烯、聚苯乙烯、纺织品、涂料等的阻燃，且具有增塑、防潮、抗静电等作用，一般TCPP由三氯氧磷和环氧丙烷按一定的比例反应所得。三（二氯丙基）磷酸酯，简称TDCP。其主要用于各种聚氨酯泡沫塑料和其他树脂，多用于软泡生产，还用于聚氯乙烯树脂、环氧树脂以及各种纤维的阻燃，且具有优良的水解稳定性、低挥发...
【技术保护点】
一种磷系阻燃剂的生产方法，其特征在于：将POCl3 及催化剂XmYn混合后无氧条件下升温至40～60℃，保温条件下滴加环氧乙烷或环氧丙烷或环氧氯丙烷，再缓慢升温至60～80℃进行老化，3小时后取老化样液测酸值为≤0.2mgKOH/g时，出料，即得磷系阻燃剂；所述催化剂XmYn为含金属及烷氧基根的催化剂，其中X为钛、锆或铝，Y为烷氧基根，m≥1，n≥1。
【技术特征摘要】
1.一种磷系阻燃剂的生产方法，其特征在于：将POCl3及催化剂XmYn混合后无氧条件下升温至40～60℃，保温条件下滴加环氧乙烷或环氧丙烷或环氧氯丙烷，再缓慢升温至60～80℃进行老化，3小时后取老化样液测酸值为≤0.2mgKOH/g时，出料，即得磷系阻燃剂；所述催化剂XmYn为含金属及烷氧基根的催化剂，其中X为钛、锆或铝，Y为烷氧基根，m≥1，n≥1。
2.根据权利要求1所述磷系阻燃剂的生产方法，其特征在于所述POCl3与催化剂X...
【专利技术属性】
技术研发人员：董晓红，房连顺，管丹，
申请(专利权)人：扬州晨化新材料股份有限公司，
类型：发明
国别省市：江苏;32