The invention discloses a wear-resistant UV curing coating for multi crack, characterized by weight portion of the raw material preparation: made of polyester acrylate urethane acrylate 13-17, three 40-46, three 9-11, trimethylolpropane acrylate silane coupling agent KH-5606-9, double 3-4, benzoin methyl ether pentaerythritol three acrylates 13-16, xylene, poly 9-12 polymethylphenylsiloxane 1-2, 10101-2, 5-7, antioxidant manganese powder corundum powder 3-4, 4-5 additives; the invention adds brown corundum powder, increase the life of the coating, wear resistance, anti cracking; adding antioxidants can prevent the formation of yellowing due to aging, cracking and other problems; adding additives, good leveling, coating uniform, good hiding power, wear resistance, aging, wide use range.
【技术实现步骤摘要】
本专利技术涉及一种涂料及其制备方法，特别是一种耐磨防裂UV固化多用涂料及其制备方法。
技术介绍
UV固化涂料已经成为较为成熟的技术，特别是随着人们环保意识的提高，生产和研究人员更加注意UV固化涂料的开发和应用。UV固化涂料是一种绿色环保型涂料，它完全符合“4E”原则，一般UV固化能耗为热固化的1/5，且UV固化涂料含挥发组分较少，污染小，最吸引研究人员和开发商的是UV固化涂料能减少原材料消耗，有利于降低经济成本。目前的UV固化材料各种各样，但是还是不同程度的存在着一些问题，现有的UV固化涂料经光固化后收缩率大、产生收缩应力,导致涂膜性脆、附着力和耐冲击力差、以及涂膜的柔韧性差和硬度低、不耐腐蚀、易黄变老化等缺点，这一系列问题都需要针对不同的用途继续改良，降低生产成本，扩大用途。
技术实现思路
本专利技术的目的是提供一种耐磨防裂UV固化多用涂料及其制备方法。为了实现本专利技术的目的，本专利技术通过以下方案实施：一种耐磨防裂UV固化多用涂料，由下列重量份的原料制备制成：聚酯丙烯酸酯40-46、氨基丙烯酸酯1...
【技术保护点】
一种耐磨防裂UV固化多用涂料，其特征在于，由下列重量份的原料制备制成：聚酯丙烯酸酯40‑46、氨基丙烯酸酯13‑17、三羟甲基丙烷三丙烯酸酯9‑11、硅烷偶联剂KH‑5606‑9、安息香双甲醚3‑4、季戊四醇三丙烯酸酯13‑16、二甲苯9‑12、聚甲基苯基硅氧烷1‑2、抗氧剂1010 1‑2、锰矿石粉5‑7、棕刚玉粉3‑4、助剂4‑5；所述助剂由下列重量份的原料制成：重晶石10‑13、竹炭5‑7、纳米二氧化硅5‑7、环氧大豆油1‑2、柠檬精油0.1‑0.2、月桂酸甲基丙烯酸酯4‑6、丙烯酸羟乙酯3‑5、硅烷偶联剂KH560 2‑3、甲基丙烯酸羟乙酯20‑24；制备方法是将重...
【技术特征摘要】
1.一种耐磨防裂UV固化多用涂料，其特征在于，由下列重量份的原料制备制成：聚酯丙烯酸酯40-46、氨基丙烯酸酯13-17、三羟甲基丙烷三丙烯酸酯9-11、硅烷偶联剂KH-5606-9、安息香双甲醚3-4、季戊四醇三丙烯酸酯13-16、二甲苯9-12、聚甲基苯基硅氧烷1-2、抗氧剂10101-2、锰矿石粉5-7、棕刚玉粉3-4、助剂4-5；
所述助剂由下列重量份的原料制成：重晶石10-13、竹炭5-7、纳米二氧化硅5-7、环氧大豆油1-2、柠檬精油0.1-0.2、月桂酸甲基丙烯酸酯4-6、丙烯酸羟乙酯3-5、硅烷偶联剂KH5602-3、甲基丙烯酸羟乙酯20-24；制备方法是将重晶石放入煅烧炉中在520-540℃下煅烧3-4...
【专利技术属性】
技术研发人员：汤广顺，
申请(专利权)人：芜湖市艾德森自动化设备有限公司，
类型：发明
国别省市：安徽;34
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。