自修复UV光固化涂料制造技术

本发明专利技术公开了自修复UV光固化涂料，属于涂料加工技术领域。它由下列重量配比的原料制成：聚酯丙烯酸树脂40%;聚氨酯丙烯酸树脂15%；自由基引发剂4%；活性单体24.5%；季戊四醇三丙稀酸酯15%；氟改性表面活性剂1%；聚醚改性硅氧烷0.5%。本发明专利技术中解决了现有技术中存在的缺点，它在涂膜成膜后，涂膜具有自修复功能。在产品使用过程中轻微划伤、刮痕、能自行修复，使涂膜表面完好如初，且不影响涂膜质感，从而延长产品使用寿命，提升外观质感。

Self repairing UV curable coating

The invention discloses a self repairing UV light curing coating, which belongs to the technical field of coating processing. It consists of the following raw materials by weight ratio: 40% polyester acrylic resin; polyurethane acrylic resin 15%; free radical initiator 4%; active monomer 24.5%; pentaerythritol three acrylates 15%; fluorinated surfactant 1%; polyether modified siloxane 0.5%. The invention solves the defects in the prior art, and the coating film has self repairing function after the coating film is formed. In the process of using products, slight scratches and scratches can be repaired automatically, so that the surface of the film is as good as before, without affecting the texture of the coating, thereby prolonging the service life of the product and enhancing the appearance and texture.

【技术实现步骤摘要】
自修复UV光固化涂料
本专利技术属于涂料加工
，具体涉及自修复UV光固化涂料。
技术介绍
涂料是一种能牢固覆盖在物体表面起保护、装饰、标志行业。现有市场上供应的UV光固化涂料，喷涂在产品上（如：手机壳，笔记本外壳，家电,电动车配套产品）如经常接触会有些表面划伤.刮痕.失光等现象.造成使用过程中不良升高。自修复UV光固化涂料是一种以聚酯丙烯酸树脂、聚氨酯丙稀酸树脂为主要成膜物质，活性单体、季戊四醇三丙稀酸酯.助剂为辅助成膜物质的功能型涂料，是目前市面上需要的一种可重涂的UV光固化涂料。
技术实现思路
本专利技术所要解决的技术问题在于提供自修复UV光固化涂料，它在涂膜成膜后，涂膜具有自修复功能。在产品使用过程中轻微划伤、刮痕、能自行修复，使涂膜表面完好如初，从而延长产品使用寿命，提升外观质感。本专利技术所要解决的技术问题采用以下技术方案来实现：自修复UV光固化涂料，由下列重量配比的原料制成：聚酯丙烯酸树脂40%;聚氨酯丙烯酸树脂15%；自由基引发剂4%；活性单体24.5%；季戊四醇三丙稀酸酯15%；氟改性表面活性剂1%；聚醚改性硅氧烷0.5%。自修复UV光固化涂料，由下列重量配比的原料本文档来自技高网...

【技术保护点】
自修复UV光固化涂料，其特征在于：由下列重量配比的原料制成：聚酯丙烯酸树脂40%;聚氨酯丙烯酸树脂15%；自由基引发剂4%；活性单体24.5%；季戊四醇三丙稀酸酯15%；氟改性表面活性剂1%；聚醚改性硅氧烷0.5%。

【技术特征摘要】
1.自修复UV光固化涂料，其特征在于：由下列重量配比的原料制成：聚酯丙烯酸树脂40%;聚氨酯丙烯酸树脂15%；自由基引发剂4%；活性单体24.5%；季戊四醇三丙稀酸酯15%；氟改性表面活性剂1%；聚醚改性硅氧烷0.5%。...