The invention relates to a combination of the two calcium silicate fused magnesia and its preparation process, wherein the fused magnesia is prepared from the following raw materials by weight percentage: 50mm < granularity less than 120mm natural magnesite block 87 ~ 96, 0mm < 4 50mm dolomite particle size less than or equal to 13 parts; power ratio CaO/SiO2 products for melting magnesium sand from 2 to 8. The invention adopts natural magnesite and dolomite block prepared by melt preparation of fused magnesia, the molar ratio between CaO/SiO2 fused magnesia in preparation of 2 ~ 8; the combination of calcium silicate is a high melting point two, thus effectively improve the material performance and high temperature resistant corrosion resistance.
【技术实现步骤摘要】
一种以硅酸二钙为结合相的电熔镁砂及其制备工艺
本专利技术涉及电熔镁砂
，尤其涉及一种以硅酸二钙为结合相的电熔镁砂及其制备工艺。
技术介绍
电熔镁砂通常用天然菱镁石或高纯轻烧镁颗粒，在埋电弧炉中熔融制得。该产品具有纯度高、结晶粒大、结构致密、抗渣性强、热震稳定性好等优点，是一种优良的高温电气绝缘材料，也是制作高档镁砖、镁碳砖及不定形耐火材料的重要原料。然而，常规生产的电熔镁砂中的CaO/SiO2的摩尔比通常在1左右，介于0.5～2.0之间，先天的化学组成决定了它的胶结相通常是低熔点的钙镁橄榄石和镁蔷薇辉石，因此该类电熔镁砂的耐高温性能和耐侵蚀性能仍然有很大的缺陷。
技术实现思路
本专利技术提供了一种以硅酸二钙为结合相的电熔镁砂及其制备工艺，采用天然菱镁矿块和白云石块为原料经熔融制备电熔镁砂，所制备的电熔镁砂中CaO/SiO2的摩尔比介于2.0～8.0之间；其结合相是高熔点的硅酸二钙，从而有效提高了材料的耐高温性能和耐侵蚀性能。为了达到上述目的，本专利技术采用以下技术方案实现：一种以硅酸二钙为结合相的电熔镁砂，由以下原料按重量份比例制成：50mm＜粒度≤120mm的...
【技术保护点】
一种以硅酸二钙为结合相的电熔镁砂，其特征在于，由以下原料按重量份比例制成：50mm＜粒度≤120mm的天然菱镁矿块87～96份，0mm＜粒度≤50mm的白云石块4～13份；电熔镁砂成品中CaO/SiO2的摩尔比为2.0～8.0。
【技术特征摘要】
1.一种以硅酸二钙为结合相的电熔镁砂，其特征在于，由以下原料按重量份比例制成：50mm＜粒度≤120mm的天然菱镁矿块87～96份，0mm＜粒度≤50mm的白云石块4～13份；电熔镁砂成品中CaO/SiO2的摩尔比为2.0～8.0。2.如权利要求1所述一种以硅酸二钙为结合相的电熔镁砂的制备工艺，其特征在于，包括如下步骤：1)原料加工；将天然菱镁矿石在破碎机中破碎，制成50mm＜粒度≤120mm粒径的天然菱镁矿块，将白云石在破碎机中破碎，制成粒径为50mm以下的白云石块；2)备料；按配比分别称取天然菱镁矿块和白云石块备用；3)熔融；采用埋弧炉对原料进行熔融；点炉前，将菱镁石块和白云石块混合后铺炉底料，炉底料高度≥500mm，以保证不烧穿炉...
【专利技术属性】
技术研发人员：张义先，董会彬，王新杰，陈东明，唐湘海，周浩，金钊，尹斌，于慧彬，赵东辉，
申请(专利权)人：海城市中兴镁质合成材料有限公司，
类型：发明
国别省市：辽宁,21