一种混凝土配方组成比例

本发明专利技术涉及一种混凝土配方，按重量分数配比由以下组分制成：水泥 100‑150 份；铁粉 5‑25 份；砂 760‑880份；粉煤灰 50‑70 份；废弃物段烧料 15‑34 份；外加剂 15‑30 份；浆水 170‑190 份；骨料 36‑85 份；超缓剂 3.85‑5.1 份；石屑 485‑520 份；碎石 1050 份 ‑1100 份。本发明专利技术的优点在于：浆水、矿粉、粉煤灰、石屑和特细砂是废料其用量在混凝土材料总量中比例达45％以上，材料成本低，降低混凝土原料成本，同时减少环境污染，低碳环保。

Concrete formula

The invention relates to a concrete formula, according to the weight fraction ratio consists of the following components made of cement 100 150 copies; 5 copies of 25 iron 760; sand 880; fly ash 50 70; section 15 34 waste material; additive 15 30; 170 190 serofluid; 36 85 aggregate; Super Retarder 3.85 5.1; stone chip 485 520 copies; 1050 copies of stone 1100 copies. The invention has the advantages of water, slag, fly ash, stone chips and fine sand is the proportion of its waste in concrete materials in the total amount of more than 45%, low material cost, reduce the cost of raw materials of concrete, and reduce environmental pollution, low carbon environmental protection.

【技术实现步骤摘要】
一种混凝土配方
本专利技术涉及混凝土制造领域，特别涉及一种混凝土配方。
技术介绍
混凝土是一种重要的基础建筑材料，其使用量巨大，而其性能又需要达到一定的标准方可安全用于相应的环境中。现在市场上的混凝土抵抗力不强，容易受环境的影响，一旦经历风吹日晒则会出现塌落、流失的危险，而混凝土又是建筑时所必须的，选择不到好的混凝土将会对后续的进展有很多的影响。
技术实现思路
本专利技术要解决的技术问题是提供一种混凝土配方，利用工业废渣来配置混凝土。为解决上述技术问题，本专利技术的技术方案为：一种混凝土配方，其创新点在于：按重量分数配比由以下组分制成：水泥100-150份；铁粉5-25份；砂760-880份；粉煤灰50-70份；废弃物段烧料15-34份；外加剂15-30份；浆水170-190份；骨料36-85份；超缓剂3.85-5.1份；石屑485-520份；碎石1050份-1100份。进一步的，所述矿粉等级为S95级以上；所述粉煤灰等级为Ⅱ级以上。进一步的，所述浆水浓度在10％-15％之间。本专利技术的优点在于：浆水、矿粉、粉煤灰、石屑和特细砂是废料其用量在混凝土材料总量中比例达45％以上，材料成本低本文档来自技高网...

【技术保护点】
一种混凝土配方，其特征在于：按重量分数配比由以下组分制成：水泥 100‑150 份；铁粉 5‑25 份；砂 760‑880份；粉煤灰 50‑70 份；废弃物段烧料 15‑34 份；外加剂 15‑30 份；浆水 170‑190 份；骨料 36‑85 份；超缓剂 3.85‑5.1 份；石屑 485‑520 份 ；碎石 1050 份 ‑1100 份 。

【技术特征摘要】
1.一种混凝土配方，其特征在于：按重量分数配比由以下组分制成：水泥100-150份；铁粉5-25份；砂760-880份；粉煤灰50-70份；废弃物段烧料15-34份；外加剂15-30份；浆水170-190份；骨料36-85份；超缓剂3.85-...

【专利技术属性】
技术研发人员：耿晓滨，
申请(专利权)人：南通不二环境科技有限公司，
类型：发明
国别省市：江苏,32