一种辅助性胶凝材料及其制备方法和用途技术
Auxiliary gelling material, preparation method and application thereof
The invention relates to an auxiliary gelling material, and also relates to a preparation method and an application of the auxiliary gelling material. The preparation method of Supplementary Cementitious Materials for (1) will be broken dolomite; (2) the accumulation of crushed dolomite pellets into the calcination equipment for calcination and insulation, calcination temperature of 800 C and 900 C, the holding time is 1H - 2H; (3) remove the calcination product cooling, grinding into powder. The auxiliary cementitious material is prepared from mortar or concrete of medium quality to replace 10% - 30% cement. The auxiliary cementitious material greatly saves the amount of cement and brings great economic effects.
【技术实现步骤摘要】
一种辅助性胶凝材料及其制备方法和用途
本专利技术涉及一种辅助性胶凝材料，还涉及该辅助性胶凝材料的制备方法和用途。
技术介绍
现今辅助胶凝材料广泛应用于水泥混凝土领域中，一些作为混合材用于制备混合硅酸盐水泥，另一些作为掺合料直接加入混凝土中，主要目的是为了改善混凝土的工作性能以及降低水泥用量。混凝土掺合料主要有工业固体废弃物和天然矿物两大类，例如粉煤灰、粒化高炉矿渣、硅灰和石灰石粉等。但随着施工工艺和设计水平的不断进步，混凝土构造物的单体规模越来越大，水泥基材料内部的温度和水分的变化引起的大体积混凝土开裂的工程事故也随之不断增多，但上述的常规掺合料并不能有效地解决水泥基材料的收缩开裂问题。目前解决水泥基材料收缩开裂常用的措施是使用膨胀水泥或直接添加具有膨胀性能的外加剂，常用的有钙矾石、氧化钙和氧化镁膨胀剂等。但钙矾石和氧化钙具有水化需水量大、水化产物物理化学性质不稳定、膨胀过程不可调控的缺点，而氧化镁膨胀剂需水量虽然相对较少，目前氧化镁膨胀剂主要用于解决大体积混凝土的温降收缩，在普通民用建筑中应用较少，并不能有效地补偿水泥基材料的早期的收缩但在制备过程中，较高的温度...
【技术保护点】
一种辅助性胶凝材料的制备方法，包括以下步骤：(1)将白云岩破碎；(2)将破碎后的白云岩粒料堆积后放入煅烧设备中进行煅烧并保温，煅烧温度为800℃—900℃，所述的保温时间为1h—2h；(3)取出煅烧产物冷却，磨制成粉末。
【技术特征摘要】
1.一种辅助性胶凝材料的制备方法，包括以下步骤：(1)将白云岩破碎；(2)将破碎后的白云岩粒料堆积后放入煅烧设备中进行煅烧并保温，煅烧温度为800℃—900℃，所述的保温时间为1h—2h；(3)取出煅烧产物冷却，磨制成粉末。2.根据权利要求1所述的辅助性胶凝材料的制备方法，其特征在于：所述的白云岩主要成分及质量含量为：MgO>20％，CaO>30％，SiO2<0.3％，Al2O3<0.7％，Fe2O3<0.4％，杂质<2％。3.根据权利要求1所述的辅助性胶凝材料的制备方法，其特征在于：破碎后的白云岩粒径小于5mm。4.根据权利要求1所述的辅助性胶凝材料的制备方法，其特征在于：煅烧的升温速率为5─66℃/min，所述的冷却方式为空气急...
【专利技术属性】
技术研发人员：邓敏，恽进进，莫立武，徐玲玲，黄晓军，江飞飞，黄蓓，
申请(专利权)人：南京工业大学，
类型：发明
国别省市：江苏,32