An airless spraying diatom mud, composed of powder weight number 800, 15 ~ 45 mesh refined diatomite, titanium dioxide, 10 ~ 20, 5 ~ 15 attapulgite, 1200 mesh wollastonite powder 5 ~ 35, superfine talc powder 5 ~ 25, 2 ~ functional materials 5, the suspension agent 2 ~ 5, 5 ~ 20 organic cementitious materials, inorganic cementitious material 10 ~ 20; when in use, according to the water powder ratio is 1.2 to 1.5: 1 mixture. The invention adopts the construction process of the base treatment + spraying the main coating, not only the construction is simple, the operation procedure is few, but also the daily construction quantity is greatly improved, and each construction worker is 400 to 600m
【技术实现步骤摘要】
一种无气喷涂硅藻泥
本专利技术涉及一种硅藻泥,具体涉及一种无气喷涂硅藻泥。
技术介绍
目前,市面上的普通硅藻泥喷花产品,在使用空压机与广口喷枪的组合时,只能采用基底处理+底涂层+喷涂主涂层+压光施工工艺,过程比较繁琐,手工艺及操作劳动量大,使得每个施工员的日施工量提升受到严重制约;同时对施工面要求严格,受每个施工员的技术功底限制,很多异形墙体结构或阴阳角施工作业比较困难,导致每个施工员日施工量少,效率低。
技术实现思路
本专利技术所要解决的技术问题是,提供一种采用基底处理+喷涂主涂层施工工艺的无气喷涂硅藻泥,有效解决了普通硅藻传统施工方法过程繁琐、异形作业面难施工、日施工量低下的问题。本专利技术解决其技术问题采用的技术方案是,一种无气喷涂硅藻泥,由以下重量份数的粉料组成,使用时,按照水∶粉料配比为1.2~1.5∶1混合制成。本专利技术硅藻土用于调节湿度,吸附有害气体甲醛等;钛白粉用于增加硅藻泥遮盖性;凹凸棒土、硅灰石粉具有较大比表面积和孔体积,吸附性强;滑石粉用于提升硅藻泥白度和润滑度。本专利技术功能性材料能使硅藻泥符合某种特殊性能,如防霉抗菌性能、降解甲醛、释放负离子等;优选光触媒、负离子材料和纳米抗菌防霉剂中的一种或两种以上的混合物。本专利技术悬浮分散助剂通过吸附于固体颗粒的表面,降低液-液或固-液之间的界面张力,使凝聚的固体颗粒表面易于湿润,体系均匀不沉淀;优选聚马来酸、聚丙烯酰胺和聚乙二醇中的一种或两种以上的混合物。本专利技术有机胶凝材料,成膜的大分子聚合物作为增强材料分布与整个砂浆体系中,从而增加了砂浆的内聚力;优选可再分散乳胶粉和/或聚乙烯醇。本专 ...
【技术保护点】
一种无气喷涂硅藻泥,其特征在于,由以下重量份数的粉料组成,800目精制硅藻土15~45份,钛白粉10~20份,凹凸棒土5~15份,1200目硅灰石粉5~35份,超细滑石粉5~25份,功能性材料2~5份,悬浮分散助剂2~5份,有机胶凝材料5~20份,无机胶凝材料10~20份;使用时,按照水:粉料配比为1.2~1.5∶1混合制成。
【技术特征摘要】
1.一种无气喷涂硅藻泥,其特征在于,由以下重量份数的粉料组成,800目精制硅藻土15~45份,钛白粉10~20份,凹凸棒土5~15份,1200目硅灰石粉5~35份,超细滑石粉5~25份,功能性材料2~5份,悬浮分散助剂2~5份,有机胶凝材料5~20份,无机胶凝材料10~20份;使用时,按照水:粉料配比为1.2~1.5∶1混合制成。2.根据权利要求1所述的无气喷涂硅藻泥,其特征在于,由以下重量份数的粉料组成,800目精制硅藻土25份,钛白粉12份,凹凸棒土5份,1200目硅灰石粉10份,超细滑石粉16份,功能性材料4份,悬浮分散助剂3份,有机...
【专利技术属性】
技术研发人员:徐正常,尹建荣,徐宗治,
申请(专利权)人:长沙洛迪环保科技有限公司,
类型:发明
国别省市:湖南,43