The invention discloses a high strength low temperature sintered glass-ceramic bond, consists of the following raw materials by weight percentage: 40 to 49%, 5 silica alumina 15%, boron oxide 8 15%, 1 5% lithium and sodium oxide, potassium oxide 6 9% 6 9% 9 12%, Magnesium Oxide, calcium oxide 11%, 5 3 barium oxide 8%, Zinc Oxide 2 5%, 3 9% P2O5 and yttrium 2 6%. The invention also discloses the preparation method and the using method of the binding agent. The invention of the glass-ceramic bond component is stable, homogeneous, easy access to various sizes of particles, and low sintering temperature, which can be achieved on the homogeneous abrasive particles wrapped in relatively low sintering temperature conditions, so as to solve the current problem of 400 # especially corundum grinding wheel with fine emery wheel in manufacturing the qualified rate of products is low, the performance is not stable.
【技术实现步骤摘要】
一种高强度低温烧结微晶玻璃结合剂及其制备方法
本专利技术涉及超硬材料制作领域，具体是一种高强度低温烧结微晶玻璃结合剂。
技术介绍
刚玉砂轮是一种常用的磨具，其制备时以刚玉磨料颗粒与结合剂混合后压制成一定形状再经高温烧结而成。砂轮的品质主要取决于结合剂本身性能的好坏以及结合剂与磨料颗粒之间的润湿性、膨胀的一致性以及结合强度等性能。因此，高性能结合剂的制备与选用是获得高性能磨具的必要条件。当前砂轮常用的结合剂有陶瓷结合剂、玻璃结合剂、树脂结合剂，以及新兴起的微晶玻璃结合剂等。其中微晶玻璃结合剂由于烧成温度低、与磨料结合强度高、热膨胀系数在一定范围内持续可调等优点成为当前研究的热点。然而，由于微晶玻璃结合剂的制备技术含量较高、工艺较为复杂、对烧结温度制度较为敏感，目前一般仍然局限于作为与金刚石及立方氮化硼等高端磨具的结合剂，很少作为刚玉砂轮用结合剂材料。如郑州大学申报的“一种低温烧结温度微晶玻璃结合剂及其制备方法(CN201610605116.7)”，该结合剂所使用的对象是金刚石磨料；“用于超硬材料砂轮的微晶玻璃结合剂及其制备方法(CN106078537A)”及“用于超...
【技术保护点】
一种高强度低温烧结微晶玻璃结合剂，其特征在于，由以下原料按照质量百分比组成：二氧化硅40‑49％、氧化铝5‑15％、氧化硼8‑15％、氧化锂1‑5％、氧化钠6‑9％、氧化钾6‑9％、氧化镁9‑12％、氧化钙5‑11％、氧化钡3‑8％、氧化锌2‑5％、五氧化二磷3‑9％和氧化钇2‑6％。
【技术特征摘要】
1.一种高强度低温烧结微晶玻璃结合剂，其特征在于，由以下原料按照质量百分比组成：二氧化硅40-49％、氧化铝5-15％、氧化硼8-15％、氧化锂1-5％、氧化钠6-9％、氧化钾6-9％、氧化镁9-12％、氧化钙5-11％、氧化钡3-8％、氧化锌2-5％、五氧化二磷3-9％和氧化钇2-6％。2.一种如权利要求1所述的高强度低温烧结微晶玻璃结合剂的制备方法，其特征在于，具体步骤如下：步骤一，按照配方称取所需原料并且过80目标准筛，将所有原料混合均匀后在1150-1350摄氏度融化形成玻璃液，保温2-4小时；步骤二，将高温玻璃液倒入室温自来水中进行水淬，经烘干和...
【专利技术属性】
技术研发人员：易晨浩，张海涛，吴敏，
申请(专利权)人：江西冠亿研磨股份有限公司，
类型：发明
国别省市：江西,36
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。