The invention relates to a method for preparing activated carbon with high specific surface area, with a hard shell as raw material, the hard shell broken to below 200 m, drying, and then added to the potassium carbonate solution for 10 15h, the hard shell and potassium carbonate solution weight ratio 1:3 5 filter; filter in the muffle furnace slag by filtering, and the CO2 gas was activated, and then cooled to room temperature, sieving, namely. The present invention has simple process, convenient operation, no equipment corrosion and environmental pollution problems, does not involve the washing and pickling process, the activated carbon with high specific surface area and developed micropore structure, with excellent adsorption performance.
【技术实现步骤摘要】
一种高比表面积活性炭的制备方法
本专利技术涉及一种活性炭的制备方法,尤其是一种高比表面积活性炭的制备方法,属于精细化工
技术介绍
活性炭是一种具有丰富孔隙结构和巨大比表面积的碳质吸附材料,它其有吸附能力强、化学稳定性好、力学强度高,且可方便再生等特点,被广泛应用于工业、农业、国防、交通、医药卫生、环境保护等领域,其需求量随着社会发展和人民生活水平提高,呈逐年上升的趋势,尤其是近年来随着环境保护要求的日益提高,使得国内外活性炭的需求量越来越大,逐年增长。而高比表面积活性炭由于具有巨大的比表面积大、化学稳定好、吸附容量大、导电性能好、再生性能较好、不溶于大多数的溶剂等优点,已广泛应用于气相吸附、液相吸附、催化反应,双电层电容器等领域。现有技术中制备高比表面积活性炭时,常要用到大量强碱,其对设备腐蚀性强,操作人员也存在安全隐患,还带来环境污染等问题。
技术实现思路
本专利技术的目的是解决现有技术中活性炭存在的不足,提供一种高比表面积活性炭的制备方法,该方法工艺简单、操作方便,工艺中不使用强碱,反应条件温和,制得的活性炭具有高的比表面积和发达的微孔结构。技术方案一种高比表面积活性炭的制备方法,包括如下步骤:(1)以硬质果壳为原料,将硬质果壳破碎至200μm以下,烘干,然后加入到碳酸钾溶液中浸泡10-15h,过滤;(2)将过滤得到的滤渣置于马弗炉中,并通入二氧化碳气体进行活化,然后冷却至室温,过筛,即得;步骤(1)中,所述硬质果壳与碳酸钾溶液的重量比为1:3-5。步骤(1)中,所述硬质果壳选自核桃壳、桃壳、杏壳、椰壳、棕榈壳等。进一步,步骤(1)中,所述碳酸钾 ...
【技术保护点】
一种高比表面积活性炭的制备方法,其特征在在于,包括如下步骤:(1)以硬质果壳为原料,将硬质果壳破碎至200μm以下,烘干,然后加入到碳酸钾溶液中浸泡10‑15h,过滤;(2)将过滤得到的滤渣置于马弗炉中,并通入二氧化碳气体进行活化,然后冷却至室温,过筛,即得;步骤(1)中,所述硬质果壳与碳酸钾溶液的重量比为1:3‑5。
【技术特征摘要】
1.一种高比表面积活性炭的制备方法,其特征在在于,包括如下步骤:(1)以硬质果壳为原料,将硬质果壳破碎至200μm以下,烘干,然后加入到碳酸钾溶液中浸泡10-15h,过滤;(2)将过滤得到的滤渣置于马弗炉中,并通入二氧化碳气体进行活化,然后冷却至室温,过筛,即得;步骤(1)中,所述硬质果壳与碳酸钾溶液的重量比为1:3-5。2.如权利要求1所述的高比表面积活性炭的制备方法,其特征在于,步骤(...
【专利技术属性】
技术研发人员:叶孙龙,
申请(专利权)人:句容市百诚活性炭有限公司,
类型:发明
国别省市:江苏,32