A method for preparing high purity ammonium polyvanadate, hydrometallurgical vanadium chemical and belongs to the technical field, wherein the method comprises the following steps: in the purification of leaching solution of NH3 containing vanadium, adjust the pH value to 4 7, stirring, filtering to obtain sodium ammonium vanadate; the ammonium vanadate sodium after water is heated and dissolved, add ammonium and adjust the pH to 2 3, to obtain high purity ammonium polyvanadate. This method has the advantages of simple process, low cost, easy operation and other advantages, the preparation of high purity ammonium polyvanadate content was greater than 90%, the vanadium yield more than 90%, with good social and economic benefits, for industrial promotion.
【技术实现步骤摘要】
一种制备高纯多钒酸铵的方法
本专利技术属于湿法冶金及钒化工
，特别涉及一种制备高纯多钒酸铵的方法。
技术介绍
多钒酸铵是一种含钒量较高的钒产品，可用于各个制钒生产领域的主要原料。尤其是制备五氧化二钒及其他氧化钒产品的原料。根据产品对氧化钒产品品质的要求，需要在钒酸铵的生产过程中控制杂质元素的进入钒酸铵固相，所以钒酸铵的品质直接决定了其他氧化钒产品的品质。专利200710201754.3提供了一种多钒酸铵的制备方法，该方法采用钙法转溶的方式得到多钒酸铵。专利201410145337.1提供了一种钒渣铵盐浸取制备偏钒酸铵的方法，该方法采用结晶得方式得到偏钒酸铵。上述多钒酸铵的制备还存在的一些问题，主要表现在：（1）钒收率较低；（2）产品杂质含量较高。因此，如何选择短流程工艺条件制备高纯多钒酸铵，是亟待解决的一个问题。通过查询相关技术可以看出，目前作为钒产品原料的钒酸铵，无论是多钒酸铵或偏钒酸铵，常规产品的生产工艺方面技术较多，但涉及铁、铬、铝等金属元素低的高纯多钒酸铵产品生产技术未见诸报道。
技术实现思路
本专利技术要解决的技术问题是一种制备高纯多钒酸铵的方法。为解...
【技术保护点】
一种制备高纯多钒酸铵的方法，其特征在于，所述方法包括以下步骤：在含钒净化浸出液中通入氨气，调节pH值至4.0‑7.0，搅拌、过滤后得到钒酸铵钠；所述钒酸铵钠加水后加热溶解，加入铵盐并调节PH值至2.0‑3.0，得到高纯多钒酸铵。
【技术特征摘要】
1.一种制备高纯多钒酸铵的方法，其特征在于，所述方法包括以下步骤：在含钒净化浸出液中通入氨气，调节pH值至4.0-7.0，搅拌、过滤后得到钒酸铵钠；所述钒酸铵钠加水后加热溶解，加入铵盐并调节PH值至2.0-3.0，得到高纯多钒酸铵。2.根据权利要求1所述的一种制备高纯多钒酸铵的方法，其特征在于，所述氨气通过微孔布气装置通入含钒净化浸出液中。3.根据权利要求2所述的一种制备高纯多钒酸铵的方法，其特征在于，所述微孔布气装置为聚四氟乙烯材质滤芯，形状为半球状。4.根据权利要求1所述的一种制备高纯多钒酸铵的方法，其特征在于，所述钒酸铵钠与水加热溶解，使溶液钒浓度达到25～40g/L。5.根据权利要求1所述的一种制备高纯多钒酸铵的方法，其特征在于，所述...