本发明专利技术涉及一种镁合金钎焊用钎料及其制备方法，属于钎焊材料技术领域。本发明专利技术的镁合金钎焊用钎料，由以下质量百分比的组分组成：42～44％Zn，1～3％Al，0.5～1.0％Sn，余量为Mg。本发明专利技术的镁合金钎焊用钎料的熔化温度范围为336～361℃，钎焊温度范围为380～400℃。在钎焊温度下，镁合金钎焊用钎料具有良好的铺展性和间隙填充性，可用于固相线温度在400℃以上的镁合金的钎焊，采用炉中钎焊工艺钎焊AZ31B镁合金接头时，钎焊对接接头抗拉强度可以达到66MPa。

Brazing filler metal for magnesium alloy and preparation method thereof

The invention relates to a magnesium alloy brazing filler metal and a preparation method thereof, belonging to the technical field of brazing materials. The brazing filler metal of the magnesium alloy of the present invention consists of the following components of mass percentage: 42 to 44%Zn, 1 to 3%Al, 0.5 to 1.0%Sn, and the margin is Mg. The melting temperature range of the brazing filler metal for magnesium alloy is 336~361 DEG C, and the brazing temperature range is 380~400 DEG C. In the brazing temperature, magnesium alloy brazing solder has a good wettability and gap filling, can be used for brazing the solidus temperature above 400 DEG C for magnesium alloy, the brazing process of AZ31B magnesium alloy in furnace brazing joints, the tensile strength of the brazing butt joint can reach 66MPa.

【技术实现步骤摘要】
一种镁合金钎焊用钎料及其制备方法
本专利技术涉及一种镁合金钎焊用钎料及其制备方法，属于钎焊材料

技术介绍
作为工业中可应用的最轻的金属结构材料，镁合金具有密度低、比强度比刚度高、导电导热性好、阻尼减振性能优异、电磁屏蔽效果佳、产品尺寸稳定、易于回收利用等优点，在航空航天、国防军工、汽车制造、电子产品等领域具有重要的应用价值和广阔的应用前景。由于产品轻量化的需求，迫切需要对应用广泛的一些镁合金进行钎焊，这就需要对镁合金钎焊所需的钎料进行研究和开发。但是，目前已获得商业化应用的镁合金钎焊钎料品种较少，且存在一些问题和不足，如含有贵重元素，导致钎料成本较高；熔化温度过高，导致钎焊温度过高；适用范围较窄，并不适于钎焊广泛应用的Mg-Al系、Mg-Zn系等镁合金。因此，在镁合金结构件焊接连接制造中，迫切需要研究和开发制备工艺简单、合金成本低、钎焊工艺性能优良、接头综合性能良好的钎料。
技术实现思路
本专利技术的目的是提供一种接头抗拉强度高的镁合金钎焊用钎料。为了实现以上目的，本专利技术的镁合金钎焊用钎料所采用的技术方案是：一种镁合金钎焊用钎料，由以下质量百分比的组分组成：42～44％Zn本文档来自技高网...

【技术保护点】
一种镁合金钎焊用钎料，其特征在于：由以下质量百分比的组分组成：42～44％Zn，1～3％Al，0.5～1.0％Sn，余量为Mg。

【技术特征摘要】
1.一种镁合金钎焊用钎料，其特征在于：由以下质量百分比的组分组成：42～44％Zn，1～3％Al，0.5～1.0％Sn，余量为Mg。2.一种如权利要求1所述的镁合金钎焊用钎料的制备方法，其特征在于：包括以下步骤：在CO2+SF6混合气体保护下，将Mg、Zn...

【专利技术属性】
技术研发人员：李萍，王莹，贺艺，赵红玲，崔扬，
申请(专利权)人：洛阳理工学院，
类型：发明
国别省市：河南,41