The invention relates to a high performance polypropylene plastic packaging barrel, which comprises the following components in parts by weight: 100 portions of polypropylene resin, polypropylene grafted maleic anhydride 2 8 zinc stearate, or N, N'ethylene bistearic amide or calcium stearate 0.5 5 copies, 1.5 copies, 0.5 coupling agent polypropylene wax 1 3 copies, 3 copies, 1 titanium dioxide brucite fiber 5 20 copies, 15 copies, 3 sepiolite fiber wollastonite fiber 3 15. The plastic packing barrel of the invention has good comprehensive performance, such as higher mechanical strength, hardness and bearing capacity, higher heat resistance, leakage prevention, antistatic property, and flame retardant effect, etc..
【技术实现步骤摘要】
一种高性能聚丙烯塑料包装桶及其制备方法
本专利技术属于塑料包装桶领域，涉及聚丙烯塑料包装桶，尤其是高性能的聚丙烯包装桶及其制备方法。
技术介绍
聚丙烯塑料包装桶美观内外光滑、无焊无缝、重量轻、强度好、耐冲击、耐腐蚀、无毒无味、运输方便，用寿命长，广泛用于涂料，润滑油，食品，化工，危包等诸多行业。而现有的聚丙烯桶存在着负载较低、易泄露、高温下容易变形、硬度偏低、高温处理后抗静电效果变差以及易燃等缺点。传统的抗静电处理方法是在塑料的组分配方中加入抗静电剂，当塑料桶在经过高温印刷步骤后，抗静电作用消失。传统抗静电剂是一种表面活性剂，具有亲水基和亲油基。和聚合物具有有限相容性，可以析出聚合物表面，亲油基植于聚丙烯树脂基体内部，亲水基伸出表面排列。亲水基可以吸附空气中的水分，形成导电溶液或自身离子化传导表面电荷，防止静电积蓄而发挥抗静电效果。由于抗静电剂属于有机小分子物质，与聚合物相容性较差，经过高温印刷容易出现析出、分解和挥发，导致印刷效能消失。高分子抗静电剂虽然可以抗高温，但是其抗静电效果较差，以及严格工艺以及结构控制给加工带来困难。海泡石纤维是一种天然矿物纤维，具有较...
【技术保护点】
一种高性能聚丙烯塑料包装桶，包括如下重量份数的组分：聚丙烯树脂100份、聚丙烯接枝马来酸酐2‑8份、硬脂酸锌或N,N'‑乙撑双硬脂酰胺或者硬脂酸钙0.5‑5份、偶联剂0.5‑2份、聚丙烯蜡1‑3份、钛白粉1‑3份、其特征在于：还包括水镁石纤维5‑20份、海泡石纤维3‑15份。
【技术特征摘要】
1.一种高性能聚丙烯塑料包装桶，包括如下重量份数的组分：聚丙烯树脂100份、聚丙烯接枝马来酸酐2-8份、硬脂酸锌或N,N'-乙撑双硬脂酰胺或者硬脂酸钙0.5-5份、偶联剂0.5-2份、聚丙烯蜡1-3份、钛白粉1-3份、其特征在于：还包括水镁石纤维5-20份、海泡石纤维3-15份。2.根据权利要求1所述的高性能聚丙烯塑料包装桶，其特征在于：还包括3-15份硅灰石纤维。3.根据权利要求1所述的高性能聚丙烯塑料包装桶，其特征在于：还包括1-3份木质纤维素。4.根据权利要求1所述的高性能聚丙烯塑料包装桶，其特征在于：还包括1-5份滑石粉、蛭...
【专利技术属性】
技术研发人员：孙金鹏，乔书强，
申请(专利权)人：天津胜威塑料有限公司，
类型：发明
国别省市：天津,12