The invention discloses a polyethylene reinforced PP filling rope, which is composed of polypropylene resin, filling master batch, defoaming agent and polyethylene resin according to weight ratio 25:75:5:4. The invention uses polypropylene resin, filler masterbatch, polyethylene resin as raw materials, improve the polyethylene enhanced PP filling rope toughness, improve the performance of tensile and compressive, tensile rate is greater than 30%, the tensile strength is 6 10N/mm, and by adding defoaming agent to further maintain the polyethylene enhanced performance of type PP filling rope. To avoid the influence of bubbles in the production process on its performance.
【技术实现步骤摘要】
一种聚乙烯增强型PP填充绳
本专利技术涉及电缆填充绳制造领域，特别涉及一种聚乙烯增强型PP填充绳。
技术介绍
电线电缆行业占据着中国电工行业1/4的产值，应用范围十分广泛，涉及到电力、建筑、通信、制造等行业，与国民经济的各个部门都密切相关。电线电缆还被称为国民经济的“动脉”与“神经”，是输送电能、传递信息和制造各种电机、仪器、仪表，实现电磁能量转换所不可缺少的基础性器材，是未来电气化、信息化社会中必要的基础产品。聚丙烯，英文名称：Polypropylene，简称聚丙烯，是由丙烯聚合而制得的一种热塑性树脂。聚丙烯由于具有优良的力学性能而被广泛用于作为电线电缆的填充物，如制造聚丙烯填充绳，但目前的聚丙烯填充绳拉伸强度不够，容易断裂，导致了用于电缆后，电缆的的圆整度和抗压抗拉能力下降，不能满足中高端电线电缆要求。
技术实现思路
本专利技术要解决的技术问题是提供一种聚乙烯增强型PP填充绳，该聚乙烯增强型PP填充绳圆整度和抗压抗拉能力强，有利于提高电缆的拉伸性能。为了解决上述技术问题，本专利技术的技术方案为一种聚乙烯增强型PP填充绳，由聚丙烯树脂、填充母料、消泡剂以及聚乙烯树脂...
【技术保护点】
一种聚乙烯增强型PP填充绳，其特征在于，由聚丙烯树脂、填充母料、消泡剂以及聚乙烯树脂按重量比25:75:5:4组成，其制备步骤如下：步骤一：在75℃的温度条件下，按比例将聚丙烯树脂、填充母料以及聚乙烯树脂在搅拌机中进行混合，搅拌20分钟，然后加入消泡剂，继续搅拌均匀后形成混合物料；步骤二：将混合物料于热挤压机的主机中进行物料软化，主机中的温度为180‑220℃，后经热挤压机的模头将软化的混合物料挤压成薄膜，模头的温度为210℃，然后经冷却液冷却进入第一牵引；步骤三：经刀片切割及拉伸板拉伸定型、干燥，进入第二牵引，拉伸板的温度为90‑100℃；步骤四：最后通过针筒打孔开网，形...
【技术特征摘要】
1.一种聚乙烯增强型PP填充绳，其特征在于，由聚丙烯树脂、填充母料、消泡剂以及聚乙烯树脂按重量比25:75:5:4组成，其制备步骤如下：步骤一：在75℃的温度条件下，按比例将聚丙烯树脂、填充母料以及聚乙烯树脂在搅拌机中进行混合，搅拌20分钟，然后加入消泡剂，继续搅拌均匀后形成混合物料；步骤二：将混合物料于热挤压机的主机中进行物料软化，主机中的温度为180-220℃，后经热挤压机的模头将软化的混合物料挤压成薄膜，模头的温度为210℃，然后经冷却液冷却进入第一牵引；步骤三：经刀片切割及拉伸板拉伸定型、干燥，进入第二牵引，拉伸板的温度为90-100℃；步骤四：最后通过针筒打孔开网，形成网状的聚乙烯增强型PP填充绳。2.根据权利要求1所述的聚乙烯增强型PP填充绳，...