The invention discloses a heat-resistant film, which relates to the technical field of plastic film products. It consists of the following parts by weight of raw materials: nitrile rubber 15 ~ 20, 20 ~ 25 of styrene butadiene rubber, nano mica powder 0.1 ~ 0.5 nanometer pine bast fiber of 0.2 ~ 0.4, 0.5 nanometer bast fiber Schima superba ~ 1, 0.2 ~ nano glass fiber 0.4, 0.4 ~ 0.8 boric acid and phosphoric acid 2 ~ 5, 1 ~ 5, the phenol curing agent 5 ~ 10, 0.5 ~ 1 and the promoter of antioxidant 1 ~ 5. The invention is mainly by adding nano mica powder, nanometer pine bast fiber and nano schimasuperba bast fiber and nano glass fiber, boric acid, phosphoric acid, phenol, heat resistance of film is improved effectively.
【技术实现步骤摘要】
耐热薄膜
本专利技术涉及塑料薄膜制品
,尤其是一种耐热薄膜。
技术介绍
薄膜是一种薄而软的透明薄片,广泛用于电子电器,机械,印刷等行业。随着科技的不断进步,人们对薄膜的关注度也越来越高,开发不同功能性质的薄膜是薄膜未来研究的方向之一。
技术实现思路
本专利技术的目的是提供一种具有耐热性能的薄膜。为了解决上述技术问题,本专利技术所采用的技术方案是:它由以下重量份的原料制成:丁腈橡胶15份~20份、丁苯橡胶20份~25份、纳米级云母粉0.1份~0.5份、纳米级红松韧皮纤维0.2份~0.4份、纳米级木荷韧皮纤维0.5份~1份、纳米级玻璃纤维0.2份~0.4份、硼酸0.4份~0.8份、磷酸2份~5份、苯酚1份~5份、硫化剂5份~10份、促进剂0.5份~1份以及防老剂1份~5份。由于采用上述技术方案,本专利技术得到的有益效果是:本专利技术主要通过加入纳米级云母粉、纳米级红松韧皮纤维、纳米级木荷韧皮纤维、纳米级玻璃纤维、硼酸、磷酸以及苯酚,从而有效的提高薄膜的耐热性能;其中,硼酸、磷酸以及甘油的加入,可以有效的缓冲高温对产物的冲击力,从而提高产物的耐热性能。具体实施方式以下结合具体实施例对本专利技术作进一步详述,而本专利技术的保护范围并非仅仅局限于以下实施例。实施例1——耐热薄膜它由以下重量的原料制成:丁腈橡胶15kg、丁苯橡胶20kg、纳米级云母粉0.1kg、纳米级红松韧皮纤维0.2kg、纳米级木荷韧皮纤维0.5kg、纳米级玻璃纤维0.2kg、硼酸0.4kg、磷酸2kg、苯酚1kg、硫化剂5kg、促进剂0.5kg以及防老剂1kg;将上述原料按照常规薄膜的制备方法进 ...
【技术保护点】
一种耐热薄膜,其特征在于由以下重量份的原料制成:丁腈橡胶15份~20份、丁苯橡胶20份~25份、纳米级云母粉0.1份~0.5份、纳米级红松韧皮纤维0.2份~0.4份、纳米级木荷韧皮纤维0.5份~1份、纳米级玻璃纤维0.2份~0.4份、硼酸0.4份~0.8份、磷酸2份~5份、苯酚1份~5份、硫化剂5份~10份、促进剂0.5份~1份以及防老剂1份~5份。
【技术特征摘要】
1.一种耐热薄膜,其特征在于由以下重量份的原料制成:丁腈橡胶15份~20份、丁苯橡胶20份~25份、纳米级云母粉0.1份~0.5份、纳米级红松韧皮纤维0.2份~0.4份、纳米级木...
【专利技术属性】
技术研发人员:谢绪金,
申请(专利权)人:柳州市乾阳机电设备有限公司,
类型:发明
国别省市:广西,45