The invention discloses a defoaming agent of high carbon alcohol and a preparation method thereof. The defoaming agent of raw materials according to the quality report containing 2 ~ 5, 0.2 ~ 0.6 palmitic acid, propylene glycol, 4 ~ 10, 6 ~ 20 octanol pentaerythritol stearate, 5 ~ 12, 12 ~ twenty-six alkanol 30 microcrystalline wax, 2.5 ~ 7.5 and 1 ~ 4 emulsifier three aluminum palmitate, and water. The defoaming agent of the invention is an emulsion containing various high carbon alcohols, and has defoaming effect. In addition, three aluminum palmitate, as hydrophobic particles, can cooperate with each other in oil phase components, which can further enhance defoaming effect. In addition, the cost is significantly reduced compared to silicone defoamer and polyether defoamer.
【技术实现步骤摘要】
高碳醇类的消泡剂及其制备方法
本专利技术消泡剂的
，尤其涉及高碳醇类的消泡剂及其制备方法。
技术介绍
在浮选、灭火、除尘、洗涤、制造泡沫陶瓷和泡沫塑料等过程中需要利用泡沫；而在发酵、涂料、造纸、印染、排除体内器官胀气、锅炉用水、废水处理及棱镜或玻璃的制造过程中需要消除泡沫，可见泡以及泡沫伴随着人们的生产和生活。所谓“泡”或“气泡”是由不溶性气体存在于液体或固体中或以它们的薄膜包围而形成的，它是一种具有气/液、气/固、气/液/固界面的分散体系，在选矿及油田体系中常见到气/液/固界面的分散气泡。许多气泡聚集在一体彼此以薄膜隔开的积聚状态称之为泡沫。泡沫的生成主要有物理法、化学法和表面活性剂法等。物理法又包括送气法(鼓泡)、溶解度降低法、加热沸腾法以及工业上常用的如振动、搅拌等起泡方法。其中送气法最为常用，技术上的关键是通过调节送气压力即可调节气泡的生成速度。一般送气速度越快，表面压力降低得越多，则气泡越易生成。缺点是送气压力大小与蒸发速度相矛盾，送气压力越低、蒸发越快。化学方法是指一切热分解反应可以产生气体的反应都可以用来起泡。例如小苏打碳酸氢钠等的加热分解以及...
【技术保护点】
一种高碳醇类的消泡剂，其特征在于，其原料按照质量份包含2～5份棕榈酸、0.2～0.6份丙二醇、4～10份正辛醇、6～20份季戊四醇酯硬脂酸酯、5～12份二十六烷醇、12～30份微晶蜡、2.5～7.5份乳化剂、1～4份三棕榈酸铝，以及水。
【技术特征摘要】
1.一种高碳醇类的消泡剂，其特征在于，其原料按照质量份包含2～5份棕榈酸、0.2～0.6份丙二醇、4～10份正辛醇、6～20份季戊四醇酯硬脂酸酯、5～12份二十六烷醇、12～30份微晶蜡、2.5～7.5份乳化剂、1～4份三棕榈酸铝，以及水。2.根据权利要求1所述的消泡剂，其特征在于，所述乳化剂为Span乳化剂、Tween乳化剂、SDS、SDBS中的一种或二种以上。3.根据权利要求1所述的消泡剂，其特征在于，所述乳化剂为由质量比为3～10:3的Tween乳化剂和SDS组成的复合乳化剂。4.根据权利要求1所述的消泡剂，其特征在于，所述水的质量份为20～50份。5.根据权利要求1所述的消泡剂，其特征在于，其原料按照质量份包含3份棕榈酸、0.4份丙二醇、6份正辛醇、12份季戊四醇酯硬脂酸酯...
【专利技术属性】
技术研发人员：李维格，钱建峰，
申请(专利权)人：苏州博纳化学科技有限公司，
类型：发明
国别省市：江苏,32