一种利用射频等离子体技术制备球形化TC4钛合金粉末的方法技术
Method for preparing spherical TC4 titanium alloy powder by radio frequency plasma technology
The invention discloses a method for preparing spherical TC4 titanium alloy powder by using radio frequency plasma technology. The method comprises the following steps: spheroidization of raw material powder of titanium alloy in plasma; obtaining spherical titanium alloy powder; the titanium alloy is TC4 titanium alloy; argon is used as the plasma. The invention adopts the RF plasma preparation method of spherical TC4 titanium alloy powder is a new technology of spheroidizing titanium alloy powder, can obtain high purity and low oxygen content, high powder spheroidization rate and good fluidity, the method is simple and easy, the production cost is lower than the traditional process, more excellent performance and can be applied to 3D printing and other fields, has good economic and social benefits, is suitable for large-scale industrialized production of spherical powder.
【技术实现步骤摘要】
一种利用射频等离子体技术制备球形化TC4钛合金粉末的方法
本专利技术涉及一种利用射频等离子体技术制备球形化TC4钛合金粉末的方法，属于功能材料制备领域。
技术介绍
TC4(Ti6Al4V)钛合金是一种高强度、耐蚀性好、耐热性高的优异功能材料，广泛应用于航空航天、医疗器件等领域。随着科学技术的发展，当今社会越来越追求高性能材料。在合金粉末领域，尤其是适于生产加工领域的高性能钛合金的材料，包括金属3D打印等方向，需要球形化的钛合金材料。为了能够实现球形化的TC4钛合金材料，众多科研工作者投入到新制备方法的研究中。目前，较为成熟的球形化TC4钛合金的制备方法包括等离子雾化法、激光烧结法、旋转电极法等。上述方法存在以下不足：(1)球形不够规则，存在椭球形粉末；(2)球化率低，存在一定量的原料粉；(3)粒度不均匀，流动性差；(4)生产效率较低，成本高不易于实现大规模生产等。目前市场上急需可用于3D打印的球化率高、流动性好的球形化钛合金材料。
技术实现思路
本专利技术的目的是提供一种利用射频等离子体技术制备球形化TC4钛合金粉末的方法，该方法制备的球形化TC4钛合金粉末具有较高的...
【技术保护点】
一种球形化钛合金粉的制备方法，包括如下步骤：将钛合金的原料粉置于等离子体中进行球化，即得到球形化钛合金粉。
【技术特征摘要】
1.一种球形化钛合金粉的制备方法，包括如下步骤：将钛合金的原料粉置于等离子体中进行球化，即得到球形化钛合金粉。2.根据权利要求1所述的制备方法，其特征在于：所述钛合金为TC4钛合金。3.根据权利要求1或2所述的制备方法，其特征在于：采用氩气作为所述等离子体。4.根据权利要求1-3中任一项所述的制备方法，其特征在于：所述球化在球化仪中进行；所述球化仪包括射频等离子体火炬；所述等离子体火炬的腔室连接一送粉器和一收集器。5.根据权利要求4所述的制备方法，其特征...
【专利技术属性】
技术研发人员：曹永革，赵翀，文子诚，麻朝阳，
申请(专利权)人：中国人民大学，
类型：发明
国别省市：北京,11