一种钢铝复合导电轨的滚压铆接制作方法，属于城市轨道交通第三轨供电用的设备。钢槽(2)的侧边的外侧冲压出与纵向中心线45°交叉的斜槽(4)，铝轨(1)的支耳(3)的对应位置滚压出包履斜槽(4)的凹槽(5)，迫使支耳(3)内侧部分铝合金材料挤入斜槽(4)的盲孔内，以滚压铆接工艺使铝轨(1)与钢槽(2)结成一体，本发明专利技术纵向与垂向钢与铝的结合力大，接触电阻小，工艺简单，生产效率高，钢槽表面无划痕，运行时电火花小，钢铝复合轨不扭曲，直线性好。

Rolling riveting method for steel aluminum composite conductive rail

The utility model relates to a rolling riveting method for a steel aluminum composite conductive rail, belonging to the equipment used for the third rail power supply of urban rail transit. Steel groove (2) side of the lateral and longitudinal center line of punch out 45 degrees cross the chute (4), (1) the aluminum rail bracket (3) corresponding to the position of roll cladding chute (4) of the groove (5), forcing the lugs (3) Aluminum Alloy inside the material part squeeze chute (4) of the blind hole, in a rolling riveting process of the aluminum rail (1) and steel groove (2) into a whole, the longitudinal and vertical steel and aluminum binding force, the contact resistance is small, simple process, high production efficiency, no scratch groove steel surface, running small spark rail, steel aluminum twist, good linearity.

【技术实现步骤摘要】
钢铝复合导电轨的滚压铆接制作方法
一种钢铝复合导电轨的滚压铆接制作方法，属于城市轨道交通第三轨供电用的设备。
技术介绍
本专利技术作出以前，在已有技术中，城市轨道交通第三轨供电的钢铝复合导电轨，其钢与铝的结合有的用冲压铆接工艺，例如专利号为201420244317.5的带燕尾槽的钢铝复合导电轨，又例如专利号为201230224323.0的钢铝复合轨，其钢槽侧边上冲裁出φ6的圆孔，然后在相应位置外侧的铝轨支耳上以φ8的冲头冲压出一凹孔，迫使部分铝合金材料挤入钢槽侧边的φ6圆孔内，使钢与铝复合成一体，这种冲压铆接工艺的难点是φ6圆孔与φ8凹孔难以保证其中心线的一致，造成钢与铝的结合力下降，并导致钢铝复合轨的扭曲，钢槽表面还留有对准用的辅助划线，运行时电火花大。
技术实现思路
本专利技术的目的在于克服上述不足之处，专利技术一种钢与铝结合力高，不会扭曲而且钢槽表面无划痕的钢铝复合导电轨。本专利技术主要解决方案是这样实现的：将不锈钢边上冲压出中心线呈±45°的小长孔，小长孔宽2mm，长约7mm，深1.5mm的盲孔；成为方向交错的斜槽(4)。然后不锈钢带进入冷弯滚压生产线折边成为15m或18m长的钢本文档来自技高网...

【技术保护点】
一种钢铝复合导电轨的滚压铆接制作方法，包括工字型的铝轨和钢槽，其特征是钢槽(2)的侧板的外侧冲压出与纵向中心线45°交叉的斜槽(4)，铝轨(1)的支耳(3)的对应位置滚压出包履斜槽(4)的凹槽(5)，迫使支耳(3)内侧部分铝合金材料挤入斜槽(4)的盲孔内。

【技术特征摘要】
1.一种钢铝复合导电轨的滚压铆接制作方法，包括工字型的铝轨和钢槽，其特征是钢槽(2)的侧板的外侧冲压出与纵向中心线45°交叉的斜槽(4)，铝轨(1)的支耳(3)的对应位置滚压出包履斜槽(4)的凹槽(5)，迫使支耳(3)内侧部分铝合金材料挤入斜槽...

【专利技术属性】
技术研发人员：李雷，
申请(专利权)人：李雷，
类型：发明
国别省市：江苏,32