The invention discloses a nano fiber reinforced fibroin film and a preparation method thereof, belonging to the field of high polymer materials. The method comprises the following steps: firstly, the PHB is dissolved in solvent to prepare the solution, dispersing carbon nanotubes in the PHB solution configuration into spinning solution; secondly, high-speed roller receiving electrostatic spinning device with high voltage static regulation range 10 ~ 20kV, 0.1 ~ 0.5ml/h injection pump flow rate, receiving distance 10 to 20cm, the drum speed is 500 ~ 2000 rpm, obtaining PHB / nano carbon nanotube nano fiber membrane; then the silk fibroin solution configuration, vacuum casting to PHB / carbon nanotube nano fiber membrane; finally, nano fiber reinforced silk fibroin film prepared by vacuum drying. The preparation method of the invention is simple, and the prepared nanofiber reinforced fibroin film has higher mechanical strength.
【技术实现步骤摘要】
一种纳米纤维增强丝素蛋白膜及其制备方法
本专利技术属于高分子材料领域，具体涉及一种纳米纤维增强丝素蛋白膜及其制备方法。
技术介绍
丝素蛋白具有优异的生物相容性，因而备受生物材料界的广泛关注，并被应用在氧渗透材料、酶固化材料及细胞培养基质中。为满足各种应用的要求，丝素蛋白需要溶解再生成薄膜及多孔支架等各种形态。天然蚕丝中的丝素蛋白具有良好的机械性能且不溶于水，而再生丝素却易于在水中溶解。为改善材料的不溶性，目前通用的方法是将再生丝素薄膜用甲醇处理，然而甲醇处理后的薄膜尽管不溶性良好，其湿态机械性能却较差，不宜作为生物材料直接应用，而同其它材料共混虽然可以改善机械性能，但却会降低材料良好的生物相容性。另一方面，经甲醇处理后残留的甲醇也会对生物体产生不良影响。因此，避免甲醇的使用并提高再生丝素蛋白薄膜的机械性能是十分必要和迫切的。近年来，纳米纤维增强复合材料的发展引起了学术界的广泛兴趣。将纳米纤维和聚合物基体结合，使纳米纤维增强复合材料的力学、热、电、生物抗菌性和防污性能得到改善，目前已有大量文献对在聚合物基体中加入纳米颗粒以提高复合材料的整体性能进行了报道，但关于使用...
【技术保护点】
一种纳米纤维增强丝素蛋白膜，其特征为，它由定向的聚羟基丁酸酯/碳纳米管纳米纤维膜与丝素蛋白溶液经真空浇注而制得。
【技术特征摘要】
1.一种纳米纤维增强丝素蛋白膜，其特征为，它由定向的聚羟基丁酸酯/碳纳米管纳米纤维膜与丝素蛋白溶液经真空浇注而制得。2.一种纳米纤维增强丝素蛋白膜的制备方法，其特征是它包括下列步骤：(1)室温下将碳纳米管分散在溶剂(I)中，碳纳米管与溶剂(I)的质量比为0.02～0.2，超声分散2h，磁力搅拌3h，配制成溶液(I)；(2)室温下将分子量为20～50万的聚羟基丁酸酯溶解于溶液(I)中，磁力搅拌6h，配制成质量体积分数为1～5％的溶液(II)(3)将溶液(II)加入到注射器中，并将其固定在微量注射泵上，采用滚筒进行接收，高压静电调节范围10～20kV，注射泵流速0.1～0.5ml/h，接收距离10～20cm，滚筒转速500～2000转/分...
【专利技术属性】
技术研发人员：蔡志江，宋现友，熊平，
申请(专利权)人：天津工业大学，
类型：发明
国别省市：天津,12