环保型纳米材料及其制备方法技术

本发明专利技术公开了一种环保型纳米材料，包括：活性炭60‑80份，蒙脱石15‑20份，纳米二氧化钛5‑10份，纳米碳化硅2‑9份，木质纤维5‑7份，云母粉2‑10份，羟丙基甲基纤维素2‑4份，聚乙烯2‑5份，硅藻土5‑7份，聚氨酯橡胶2‑8份。本发明专利技术材料中含有大量的活性炭，具有较高的吸附能力，满足环保型材料的要求；在材料中添加木质纤维，减轻材料的重量；在材料中添加了聚氨酯橡胶，使得材料耐磨性能较好，并且具有耐老化、气密性好的优良特性。

Environmental protection type nano material and preparation method thereof

The present invention discloses a kind of environmental friendly nano materials, including: activated carbon 60 80 copies, 20 copies of the 15 montmorillonite nano titanium dioxide, 5 10 copies, 2 Nano SiC wood fiber 5 9 copies, 7 copies, 10 copies of 2 mica powder, hydroxypropyl methyl cellulose 2 4, polyethylene 2 5 copies, 7 copies of the 5 diatomite, polyurethane rubber 8 2. The material of the invention contains a large number of activated carbon, the adsorption capacity is higher, meet environmental protection material requirements; add wood fiber in the material, reduce the weight of the material; adding polyurethane rubber in the material, the wear resistance of material is good, and has excellent resistance to aging properties, good air tightness.

【技术实现步骤摘要】
环保型纳米材料及其制备方法
本专利技术涉及建筑材料领域，具体涉及一种生物环保型纳米材料及其制备方法。
技术介绍
新型建筑材料品种众多，形式各异，具有经济实用、市场环保的优点，能够满足现代建筑装饰审美的要求。随着建筑材料的不断创新，现在常用的新型建筑材料有：新型墙体材料、保温隔热材料、防水密封材料等等。随着建筑市场的要求越来越高，建筑材料的质量也要求越来越高。现在建筑材料不但要求具有较好的综合性能，还要求具有环保性能，能够减少环境污染。
技术实现思路
本专利技术的目的在于克服现有技术存在的以上问题，提供一种绿色环保纳米材料。为实现上述技术目的，达到上述技术效果，本专利技术通过以下技术方案实现：一种环保型纳米材料，按照重量份数计，包括：优选地，包括：优选地，所述纳米二氧化钛的粒径为20-100nm。优选地，所述纳米碳化硅的粒径为10-50nm。优选地，所述木质纤维的长度为1-3cm。优选地，一种制备环保型纳米材料的方法，包括以下步骤：S101按照配方中各组分的比例备料；S102将粉末状的组分混合均匀，过400目筛，然后加入木质纤维，混合均匀；S103将制备得到的混合均匀后的混合物注入到成型模本文档来自技高网...

【技术保护点】
一种环保型纳米材料，其特征在于，按照重量份数计，包括：

【技术特征摘要】
1.一种环保型纳米材料，其特征在于，按照重量份数计，包括：2.根据权利要求1所述的环保型纳米材料，其特征在于，按照重量份数计，包括：3.根据权利要求1所述的环保型纳米材料，其特征在于，所述纳米二氧化钛的粒径为20-100nm。4.根据权利要求1所述的环保型纳米材料，其特征在于，所述纳米碳化硅的粒径为10-50nm。5.根据权利要求1所述的环保型纳米材料，其特征在于，所述木质纤维的长度为1-3cm。6.一种制备权利要求1-5任意一项中所述的环保型纳米材料的方法，其...

【专利技术属性】
技术研发人员：张晓辉，
申请(专利权)人：佛山市蓝瑞欧特信息服务有限公司，
类型：发明
国别省市：广东,44