The invention discloses a method for preparing magnesium hydrogen phosphate hydroxyapatite core-shell materials, under the normal temperature, adjusting two hydrogen phosphate magnesium solution with saturated calcium hydroxide solution of pH 6 8, after the complete reaction filtering and washing, then magnesium hydrogen phosphate hydroxyapatite core-shell materials in 90 drying at 180 deg.C. The magnesium hydrogen phosphate hydroxyapatite core shell material prepared by the invention has the advantages of uniform particle size and controllable particle size, simple and easy reaction process, low energy consumption and low cost, and is suitable for large-scale industrial production.
【技术实现步骤摘要】
一种磷酸氢镁羟基磷灰石核壳材料的制备方法
本专利技术属于核壳材料的合成
，具体涉及一种磷酸氢镁羟基磷灰石核壳材料的制备方法。
技术介绍
磷酸氢镁在医药上用作变质剂和制造治疗风湿性关节炎的药物。食品行业中用于营养增补剂、pH调节剂、拮抗剂和稳定剂。另外还用于包装材料增塑剂、化肥碳酸氢铵稳定剂、牙膏添加剂，也可以用作饲料添加剂和肥料。在城市及工业污水处理中被用作化学沉淀剂，因为磷酸氢镁能与铵离子反应形成磷酸镁铵，所以用于去除浓度较高的水体富营养化污染-氨氮。单独使用磷酸氢镁有许多缺点，如在医药、食品领域由于镁离子与钙离子半径相近，在镁离子进入人体后对中枢神经有抑制作用，在磷酸氢镁外面包覆一层羟基磷灰石壳可以有效避免镁离子进入人体，而羟基磷灰石是人体骨骼的主要成分，对人体无害。在污水处理时磷酸氢镁与铵离子反应生成磷酸氢镁，磷酸氢镁在水中具有一定的溶解性，所以其对氨氮的处理只能用于高浓度氨氮污水，而且处理达不到排放标准，而在磷酸氢镁外面包覆一层羟基磷灰石壳可以阻止磷酸镁铵的溶解，所以磷酸氢镁羟基磷灰石核壳材料在氨氮污水处理时具有很好的性能。目前尚没有关于磷酸氢镁羟基...
【技术保护点】
一种磷酸氢镁羟基磷灰石核壳材料的制备方法，其特征在于具体步骤为：在常温常压下，用饱和氢氧化钙溶液调节磷酸二氢镁溶液的pH为6‑8，反应完全后过滤水洗，再于90‑180℃干燥得到磷酸氢镁羟基磷灰石核壳材料。
【技术特征摘要】
1.一种磷酸氢镁羟基磷灰石核壳材料的制备方法，其特征在于具体步骤为：在常温常压下，用饱和氢氧化钙溶液调节磷酸二氢镁溶液的pH为6-8，反应完全后过滤水洗，再于90-180℃干燥...
【专利技术属性】
技术研发人员：王魁，杨林，王晓兵，刘自力，李伟，
申请(专利权)人：河南师范大学，
类型：发明
国别省市：河南,41
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。