The invention discloses a refractory refractory adhesive glue and its producing method, according to the weight percentage, from 50 60% phosphoric acid, aluminum hydroxide 20 30% alpha Al2O3 powder 0 10%, 0 zirconia silica 5%, 0 and 10 5%, water 20%. This invention relates to a manufacturing method of refractory adhesive, which comprises the following steps: 1) adding water solution of phosphoric acid concentration of 85%, heating to 100 DEG C 150 DEG C; 2) the aluminum hydroxide, zirconium oxide, silicon dioxide, and alpha Al2O3 powder added in step 1) in phosphoric acid solution, stirring until the solution without sediment 3); step 2) the solution is cooled to room temperature. Refractory adhesive obtained by the invention has the advantages of early, high bonding strength and good temperature resistance, the maximum temperature reached 1600 degrees above, suitable refractories for making high temperature environment with clay, long service life.
【技术实现步骤摘要】
一种耐火胶及其制造方法
本专利技术涉及耐火材料
，特别涉及一种耐火胶及其制造方法。
技术介绍
目前市场上的PA胶、KP胶等最高使用温度一般在1000℃-1350℃之间，其耐高温效果还不够理想，用其作为高温环境下使用的耐火材料砌筑用胶泥，容易出现砌筑材料松动脱落的问题，使用寿命较短。
技术实现思路
有鉴于此，本专利技术的目的是提供一种耐火胶及其制造方法，以解决现有PA胶、KP胶等的耐高温性能还不够好的技术问题。本专利技术耐火胶，按重量百分比计，由如下配料组成：磷酸50-60％，氢氧化铝20-30％，α-Al2O3微粉0-10％，氧化锆0-5％，二氧化硅0-5％，水10-20％；所述磷酸为85％浓度的磷酸溶液；所述氢氧化铝、氧化锆、二氧化硅、α-Al2O3均为325目以上的细粉。本专利技术还公开了耐火胶的制造方法，其包括以下步骤：1)将水加入85％浓度的磷酸溶液中，加热至100℃-150℃；2)将氢氧化铝、氧化锆、二氧化硅、以及α-Al2O3微粉加入步骤1)中的磷酸溶液中，搅拌至溶液内无沉淀物，在搅拌过程中保持溶液温度在100℃-150℃之间；3)将步骤2)获得的溶...
【技术保护点】
一种耐火胶，其特征在于：按重量百分比计，由如下配料组成：磷酸50‑60％，氢氧化铝20‑30％，α‑Al2O3微粉0‑10％，氧化锆0‑5％，二氧化硅0‑5％，水10‑20％；所述磷酸为85％浓度的磷酸溶液；所述氢氧化铝、氧化锆、二氧化硅、α‑Al2O3均为325目以上的细粉。
【技术特征摘要】
1.一种耐火胶，其特征在于：按重量百分比计，由如下配料组成：磷酸50-60％，氢氧化铝20-30％，α-Al2O3微粉0-10％，氧化锆0-5％，二氧化硅0-5％，水10-20％；所述磷酸为85％浓度的磷酸溶液；所述氢氧化铝、氧化锆、二氧化硅、α-Al2O3均为325目以上的细粉。2.一种权利要求1...
【专利技术属性】
技术研发人员：李兴，杜春天，谢俊平，张泽，甘乐才，谭春凡，江琴，
申请(专利权)人：重庆钢铁集团矿业有限公司冶金材料厂，
类型：发明
国别省市：重庆,50
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。