一种发射增强的荧光粉的制备方法技术
Method for preparing emission enhanced fluorescent powder
The invention provides a preparation method of fluorescent powder emission enhancement, the use of metal powder as reducing agent, metal powders of Al, Ti or Mg, Ca2SiO4:Eu precursor containing in the first quartz glass tube, reducing agent and quality Ca2SiO4:Eu powder ratio (0.05 ~ 1): 1, then the first will be put on the bottom of quartz glass tube filled with metal powder second quartz glass tube, quartz glass tube sealing machine second vacuum seal using oxyhydrogen flame, and in the muffle furnace, in 600 under 1000 DEG C, heat treatment 6~10h, the emission enhancement of Ca2SiO4:Eu phosphor. The Ca2SiO4:Eu powder prepared by the invention is 2.8 times as good as the emission intensity of the Ca2SiO4:Eu powder prepared by the CO reducing agent.
【技术实现步骤摘要】
一种发射增强的荧光粉的制备方法
本专利技术属于化工领域，涉及一种荧光粉，具体来说是一种发射增强的荧光粉的制备方法。
技术介绍
白光LED是一种新型固态照明光源，与传统的白炽灯、荧光灯相比，具有功耗小、效率高、绿色环保、节能、寿命长、体积小、响应快、显色性好等显著优点，成为新一代绿色环保照明光源，具有广阔的市场前景和巨大的社会经济效益，已得到业界的广泛关注。目前，基于LED产生白光发射的方式主要有3种：(1)多色组合法，即通过红色、绿色、蓝色三色混合产生白光，如组合红，绿，蓝(RGB)三色发光二极管；(2)使用紫外LED激发RGB荧光粉；(3)使用蓝色发光二极管激发黄色荧光粉。其中，以紫外LED激发RGB荧光粉的组合方案显色性能最佳，但是由于视觉对紫外-近紫外光的不敏感性，这类白光LED的颜色只由荧光粉决定，因此研发可用于近紫外(350～420nm)型白光LED(NUV-LED)用的三基色荧光粉显得尤为重要。Ca2SiO4:Eu2+绿色荧光粉由于激发波长范围宽、发光亮度高、化学稳定性好等优点，而被国内外的研究学者广泛研究。如研究学者通过固相反应法，溶胶-凝胶法，共沉...
【技术保护点】
一种发射增强的荧光粉的制备方法，其特征在于：使用金属单质粉末为还原剂，所述的金属单质粉末为Al，Ti或Mg，将Ca2SiO4:Eu前驱体盛放于第一石英玻璃管中，所述的还原剂与Ca2SiO4:Eu粉的质量比为（0.05～1）∶1 ，然后将第一石英玻璃管放于底部盛有金属单质粉末的第二石英玻璃管中，所述的第二石英玻璃管的直径大于所述的第一石英玻璃管的直径，使用氢氧焰密封机将第二石英玻璃管抽真空后密封，并置于马弗炉中，在600‑1000℃条件下，进行加热处理6~10h，即得发射增强的Ca2SiO4:Eu荧光粉。
【技术特征摘要】
1.一种发射增强的荧光粉的制备方法，其特征在于：使用金属单质粉末为还原剂，所述的金属单质粉末为Al，Ti或Mg，将Ca2SiO4:Eu前驱体盛放于第一石英玻璃管中，所述的还原剂与Ca2SiO4:Eu粉的质量比为（0.05～1）∶1，然后将第一石英玻璃管放于底部盛有金属单质粉末的第二石英玻璃管中，所述的第二石英玻璃管的直径大于所述的第一石英玻璃管的直径，使用氢氧焰...
【专利技术属性】
技术研发人员：侯京山，随大友，房永征，刘玉峰，赵国营，蒋广翔，郑新峰，
申请(专利权)人：上海应用技术大学，
类型：发明
国别省市：上海,31