一种使用六甲基磷酰三胺阻燃的PVC配方组成比例

本发明专利技术公开了一种使用六甲基磷酰三胺阻燃的PVC配方，其特征在于由下列重量份的原料制成：PVC树脂60‑100份，邻苯二甲酸二辛酯4‑7份，氧化锌2‑7份，六甲基磷酰三胺6‑8份，油酸酰胺1‑2份，氯化石蜡2‑3份，助剂0.5‑1.3份。本发明专利技术的有益效果是：利用该配方制造出来的PVC管材可以增强抗冲性能及强度，添加的六甲基磷酰三胺，不但可以大大提高PVC管材的抗氧化性能，而且成比较低，适合推广应用。

A PVC formulation using six methyl phosphorous three amine flame retardant

The invention discloses a formula of PVC using six methyl three phosphoryl amine flame retardant, which is characterized in that the weight made of the following raw materials: PVC resin 60 100, adjacent benzene two formic acid two - 4 7, Zinc Oxide 2 7 copies, six methyl three phosphoryl amine 6 8 copies. 1 oleic acid amide 2, chlorinated paraffin 2 3 copies, 1.3 copies of 0.5 additives. The beneficial effect of the invention is: PVC pipe manufactured using this formula can enhance the anti impact performance and strength, adding six methyl three phosphoryl amine, not only can greatly improve the oxidation resistance of the PVC pipe, and a relatively low, suitable for application.

【技术实现步骤摘要】
一种使用六甲基磷酰三胺阻燃的PVC配方
本专利技术涉及塑胶管道
，具体涉及一种使用六甲基磷酰三胺阻燃的PVC配方。
技术介绍
PVC管材的主要成分是聚氯乙烯，另外加入其它成分来增强其耐热性、韧性、延展性等。PVC在当今世界上深受喜爱，是颇为流行并广泛应用的一种合成材料。PVC管材是一种成熟的管材，主要应用于给排水工程。PVC管材具有耐酸、耐碱、耐腐蚀、强度高等优点，但抗冲性能比较差。
技术实现思路
本专利技术提供一种使用六甲基磷酰三胺阻燃的PVC配方，利用该配方制造出来的PVC管材可以增强抗冲性能及强度。为达到上述目的，本专利技术一种使用六甲基磷酰三胺阻燃的PVC配方，其特征在于由下列重量份的原料制成：PVC树脂60-100份，邻苯二甲酸二辛酯4-7份，氧化锌2-7份，六甲基磷酰三胺6-8份，油酸酰胺1-2份，氯化石蜡2-3份，助剂0.5-1.3份。作为优选，由下列最优配比原料制成：PVC树脂80份，邻苯二甲酸二辛酯3.7份，氧化锌4份，六甲基磷酰三胺7份，油酸酰胺1.4份，氯化石蜡2.6份，助剂0.6份。作为优选，助剂为增塑剂、润湿剂、稳定剂中的一种或两种以上组成。本专利技术的有本文档来自技高网...

【技术保护点】
一种使用六甲基磷酰三胺阻燃的PVC配方，其特征在于由下列重量份的原料制成：PVC树脂60‑100份，邻苯二甲酸二辛酯4‑7份，氧化锌2‑7份，六甲基磷酰三胺6‑8份，油酸酰胺1‑2份，氯化石蜡2‑3份，助剂0.5‑1.3份。

【技术特征摘要】
1.一种使用六甲基磷酰三胺阻燃的PVC配方，其特征在于由下列重量份的原料制成：PVC树脂60-100份，邻苯二甲酸二辛酯4-7份，氧化锌2-7份，六甲基磷酰三胺6-8份，油酸酰胺1-2份，氯化石蜡2-3份，助剂0.5-1.3份。2.如权利要求1所述的一种使用六甲基磷酰三胺阻燃的PVC配方...