The invention discloses a ceramic fiber reinforced three EPDM material, made from the following materials by weight: three EPDM 100, ceramic fiber 20~30, silica 20~40, stearic acid 0.5~1, 1~2, accelerator TMTD KH550 1, DCP is 1~2. The invention adds ceramic fiber in three EPDM rubber in the body, effectively reducing the amount of carbon containing materials, adding other non-metallic material proportion, therefore, in an oxygen rich environment, can greatly increase the erosion resistance, normal work for rocket engine. KH 550 to join, is conducive to the compatibility between the ceramic fiber and silica, three yuan of ethylene propylene rubber. The ceramic fiber reinforced three yuan EPDM rubber has good mechanical properties and low wire erosion rate. It has good service performance and stable quality. It can meet the requirements of actual R & D and production.
【技术实现步骤摘要】
一种陶瓷增强三元乙丙橡胶材料及制备方法
本专利技术属于固体火箭发动机绝热材料
，具体涉及一种陶瓷纤维增强三元乙丙橡胶材料及制备方法。
技术介绍
固体火箭发动机通常多采用传统的橡胶基绝热材料，为了解决材料边分解边剥落、无法形成材料碳化层的问题，开发了定长碳纤维(平铺)增强酚醛改性丁腈橡胶绝热材料以及编织碳纤维增强酚醛改性丁腈橡胶绝热材料。该类材料性能优越，但随着发动机性能的提高，尤其在富氧环境的工作，碳纤维容易氧化和燃烧，降低了其耐烧蚀性能。
技术实现思路
本专利技术的目的提供一种陶瓷纤维增强三元乙丙橡胶材料及制备方法，以解决其在富氧环境下容易氧化和燃烧的难题、达到提高其耐烧蚀性能的目的。为解决上述技术问题，本专利技术所采用的技术方案是：一种陶瓷纤维增强三元乙丙橡胶材料，采用按重量份计的以下材料制成：三元乙丙橡胶为100份、陶瓷纤维为20～30份，白炭黑为20～40份、硬脂酸为0.5～1份、促进剂TMTD为1～2份、KH550为1份、DCP为1～2份。优选的方案中，三元乙丙橡胶为100份、陶瓷纤维为25-28份，白炭黑为25-35份、硬脂酸为0.5～1份、促进剂T...
【技术保护点】
一种陶瓷纤维增强三元乙丙橡胶材料，其特征在于，采用按重量份计的以下材料制成：三元乙丙橡胶为100份、陶瓷纤维为20~30份，白炭黑为20~40份、硬脂酸为0.5~1份、促进剂TMTD 为1~2份、KH550为1份、DCP为1~2份。
【技术特征摘要】
1.一种陶瓷纤维增强三元乙丙橡胶材料，其特征在于，采用按重量份计的以下材料制成：三元乙丙橡胶为100份、陶瓷纤维为20~30份，白炭黑为20~40份、硬脂酸为0.5~1份、促进剂TMTD为1~2份、KH550为1份、DCP为1~2份。2.根据权利要求1所述的材料，其特征在于：三元乙丙橡胶为100份、陶瓷纤维为25-28份，白炭黑为25-35份、硬脂酸为0.5~1份、促进剂TMTD为1~2份、KH550为1份、DCP为1~2份。3.根据权利要求1所述的材料，其特征在于：所述陶瓷纤维为硅酸铝纤维，且含富氧化锆。4.根据权利要求1所述的材料，其特征在于：所述陶瓷纤维的直径控制在20~30um。5.权利要求1-4任意一项所述材料的制备方法，其特征在于，具体步骤为：1）采用开练机对三元...
【专利技术属性】
技术研发人员：朱稼麟，刘美珍，李方朔，陈永钊，崔峰，曾庆江，贾冬梅，刘松华，张华燕，张浩，吴斌，
申请(专利权)人：湖北三江航天江河化工科技有限公司，
类型：发明
国别省市：湖北,42