一种基于有机稀土材料为主的复合催化剂以及塑胶跑道用胶粘剂制造技术

本发明专利技术公开了一种基于有机稀土材料为主的复合催化剂以及塑胶跑道用胶粘剂，其技术方案要点是包括如下重量份的组分：异辛酸稀土10~15份；异辛酸锌5~8份；异辛酸铋3~5份；气相白炭黑10~15份；聚醚多元醇57~72份；本申请将上述异辛酸稀土、异辛酸锌、异辛酸铋、气相白炭黑与聚醚多元醇进行混合，制备的复合催化剂是一种新型环保塑胶跑道用催化剂，是现有技术中的环保型的催化剂的替代产品，具有优异的安全、环保的使用性。

Composite catalyst based on organic rare earth material and adhesive for plastic runway

The invention discloses an organic adhesive for rare earth materials based on composite catalyst and plastic runway, the technological scheme includes the following components by weight: ISOOCTOATE rare-earth 10~15; isooctanoate zinc 5~8; isooctanoate bismuth 3~5; fumed silica 10~15; polyether polyol 57~72; the application of the above ISOOCTOATE rare-earth, isooctanoate zinc, isooctanoate bismuth, fumed silica and polyether polyols were mixed for preparing composite catalyst is a catalyst for a new type of environmental friendly plastic runway, is catalytic in the prior art agent substitute products, use has excellent safety and environmental protection the.

【技术实现步骤摘要】
一种基于有机稀土材料为主的复合催化剂以及塑胶跑道用胶粘剂
本专利技术涉及催化剂，特别涉及一种基于有机稀土材料为主的复合催化剂以及塑胶跑道用胶粘剂。
技术介绍
自第19届奥林匹克运动会时国际奥委会决定正式采用聚氨酯塑胶跑道作为国际赛事的设施，自此打开了聚氨酯塑胶跑道的新局面，聚氨酯塑胶运动场在全世界得到了空前的普及。特别是近十年来，随着我国全民健身运动的开展以及人民生活水平的提高，越来越多的各级学校和公共运动场所铺设或正在铺设聚氨酯跑道，聚氨酯塑胶跑道正呈蓬勃发展之势。最近，不乏从媒体上能够看到一些塑胶跑道的负面报道。报道称，某地多所学校出现“毒塑胶跑道”导致学生出现流鼻血、头晕、皮肤过敏等症状的消息持续发酵，相关部门对出现事故学校的塑胶跑道也做了大量的质检。结果表明，塑胶跑道经过空气的暴晒、雨水的冲刷会向空气中散发挥发性物质，学生吸入大量挥发性物质导致了流鼻血、头晕、皮肤过敏等现象，这引起了社会的广泛关注。毒塑胶跑道中通常采用含铅、汞的有害重金属的材料作为催化剂，并且一般催化剂中含有50％以上的芳烃溶剂，而申请公布号为CN106433547A的中国专利公开了一种改性聚氨酯胶黏剂及其制本文档来自技高网...

【技术保护点】
一种基于有机稀土材料为主的复合催化剂，其特征在于包括如下重量份的组分：

【技术特征摘要】
1.一种基于有机稀土材料为主的复合催化剂，其特征在于包括如下重量份的组分：2.根据权利要求1所述的一种基于有机稀土材料为主的复合催化剂，其特征在于：所述聚醚多元醇的分子量为4000～4200。3.根据权利要求2所述的一种基于有机稀土材料为主的复合催化剂，其特征在于：所述气相白炭黑的比表面积为400～430m2/g。4.根据权利要求1所述的一种基于有机稀土材料为主的复合催化剂，其特征在于：还包括异辛酸锆6～10份。5.根据权利要求4所述的一种基于有机稀土材...

【专利技术属性】
技术研发人员：潘毅，
申请(专利权)人：江苏耐斯坦铺装材料有限公司，
类型：发明
国别省市：江苏,32