The invention relates to a glaze, particularly relates to a method for preparing jujube red matte glaze. The technical scheme comprises the following steps: (1) preparation of raw materials: the mineral raw materials by grinding filtration, prepared particle size in the raw material particles below 200 mesh; (2) the raw material particles below 200 mesh, according to the weight ratio of 2 to 5, 2 to 5 portions of manganese carbonate manganese oxide, 3 ~ 10 and 3 ~ 10 talc chlorite mixed evenly, add appropriate amount of water stir mud like filtering, prepare glaze; (3): (4) heating hanging glaze firing. This invention provides a preparation method of purplish red matte glaze, raw materials entirely from natural minerals, does not add any pigment and additives can improve the intrinsic value of mineral materials, provides a new way of mineral resources, provide a new resource for industrial ceramic glaze.
【技术实现步骤摘要】
一种枣红色哑光釉料的制备方法
本专利技术涉及一种釉，具体涉及一种枣红色哑光釉料的制备方法。
技术介绍
我国是矿业大国，目前矿产资源还处在提高利用率的过程中，矿产资源利用率还有很大的上升空间。许多常见的非金属资源储量丰富，目前还没有被有效、充分利用，其所潜在的经济价值还有待挖掘。因此，矿物资源高效利用仍然是个热点问题，引起社会重视。我国是个陶瓷大国，国内外对各类陶瓷产品，尤其是具有中国风格的陶瓷产品需求量很大，这使得对陶瓷制品所需的釉面材料的多样性、稳定性要求越来越高。而现阶段，大多数色釉都是在基础釉的基础上，加入适量的金属氧化物或碳酸盐进行调色。这一过程限制了釉面材料的多样性，同时所需的着色氧化剂是经过二次加工的产物，增加了整个过程的能耗，制约了我国陶瓷产业的发展。研究发现，天然矿物中长石、白云石、石英、滑石、方解石、透辉石、绿泥石、硅灰石、绿帘石及少量闪石、云母类矿物等，这些物质都是制备陶瓷材料的重要成分。并且这些矿物所含多种致色离子，为获得多色性釉料提供了可能。
技术实现思路
本专利技术提供一种枣红色哑光釉料的制备方法，原料完全取自天然矿物，不添加任何色料和助剂，...
【技术保护点】
一种枣红色哑光釉料的制备方法，其特征在于，包括如下步骤：(1)原料制备：所用的矿物原料包括：碳酸锰、氧化锰、滑石、绿泥石；将所用的矿物原料经粉碎研磨过滤，制得粒径在200目以下的原料颗粒；(2)釉料制备：将200目以下的原料颗粒，按照重量比取2～5份碳酸锰、2～5份氧化锰、3～10份滑石和3～10份绿泥石均匀混合，加入适量的水搅拌呈泥浆状过滤，制得釉料；(3)挂釉：陶质试片表面经除尘、水润处理之后，将所述釉料均匀喷洒在陶质试片表面，并静置5～10分钟；(4)加温烧制：将挂釉后的陶质试片放置电窑中，加温烧制，烧制温度240～1300℃，烧制时间8～10小时，自然冷却至室温。
【技术特征摘要】
1.一种枣红色哑光釉料的制备方法，其特征在于，包括如下步骤：(1)原料制备：所用的矿物原料包括：碳酸锰、氧化锰、滑石、绿泥石；将所用的矿物原料经粉碎研磨过滤，制得粒径在200目以下的原料颗粒；(2)釉料制备：将200目以下的原料颗粒，按照重量比取2～5份碳酸锰、2～5份氧化锰、3～10份滑...