The present invention provides a method for 3D printing materials of high toughness heat-resistant tube, its components and components for quality copies are: clay base: 32 ~ 46, 15 ~ 27: silicate fiber reinforced substrate, 16 to 23, 10 to 23 parts: auxiliary agent; auxiliary agent ingredients and components for auxiliary agent respectively: silica aerogels: 7 - 11, Aluminium Phosphate Gel: acidic water solution 3 ~ 5, TEOS: 3 - 5, 2 - 5, stabilizer: toughening agent: 2 - 4, dispersant: 2 - 4, 1 to 3 parts: adhesive. The invention adopts the unique composition composition of 3D printing materials, applicable to the needs of the heat pipe has the toughness of 3D printing production, the finished pipe to ensure the mechanical properties at the same time, also has excellent toughness and temperature capability.
【技术实现步骤摘要】
一种用于高韧性耐热管件的3D打印材料
本专利技术属于精密铸造工艺领域，具体涉及一种用于高韧性耐热管件的3D打印材料。
技术介绍
随着工业生产的飞速发展，管件逐渐应用于各种环境中，对于管件的各项性能需求也在逐渐提升。对于应用于高温环境中的管件，在保证其具有优良机械性能的同时，还需要具有优秀的承温能力，对于一些具有形状、尺寸要求的管件，其制作精度也要求较高；同时为了防止由于撞击等因素造成管件的开裂损坏，管件自身的韧性也具有一定要求。因此，为了解决以上问题研制出一种高韧性，且耐热性能优秀的管件材料是本领域技术人员所急需解决的难题。
技术实现思路
为解决上述问题，本专利技术公开了一种用于高韧性耐热管件的3D打印材料。为了达到上述目的，本专利技术提供如下技术方案：一种用于高韧性耐热管件的3D打印材料，其组成成分以及各成分所占质量份数分别为：粘土基底：32～46份、硅酸盐纤维：15～27份、增强基底：16～23份、辅助剂：10～23份；辅助剂的组成成分以及各成分所占辅助剂质量份数分别为：二氧化硅气凝胶：7～11份、磷酸铝凝胶：3～5份、正硅酸乙酯的酸性水溶液：3～5份、稳定剂：2...
【技术保护点】
一种用于高韧性耐热管件的3D打印材料，其特征在于：其组成成分以及各成分所占质量份数分别为：粘土基底：32～46份、硅酸盐纤维：15～27份、增强基底：16～23份、辅助剂：10～23份；所述辅助剂的组成成分以及各成分所占辅助剂质量份数分别为：二氧化硅气凝胶：7～11份、磷酸铝凝胶：3～5份、正硅酸乙酯的酸性水溶液：3～5份、稳定剂：2～5份、增韧剂：2～4份、分散剂：2～4份、胶粘剂：1～3份。
【技术特征摘要】
1.一种用于高韧性耐热管件的3D打印材料，其特征在于：其组成成分以及各成分所占质量份数分别为：粘土基底：32～46份、硅酸盐纤维：15～27份、增强基底：16～23份、辅助剂：10～23份；所述辅助剂的组成成分以及各成分所占辅助剂质量份数分别为：二氧化硅气凝胶：7～11份、磷酸铝凝胶：3～5份、正硅酸乙酯的酸性水溶液：3～5份、稳定剂：2～5份、增韧剂：2～4份、分散剂：2～4份、胶粘剂：1～3份。2.根据权利要求1所述的一种用于高韧性耐热管件的3D打印材料，其特征在于：所述粘土基底的组成成分以及各成分所占质量份数分别为：木节粘土：13～21份、油粘土：7～11份、膨润土：5～9份。3.根据权利要...