一种耐高温含硅氧烷芳炔树脂泡沫材料制造技术
A high temperature resistant silicone containing aramid resin foam material
The invention discloses a high temperature resistant silicone containing arylacetylene resin foam material, which is characterized in that the material consists of silicone containing arylacetylene resin 110, foaming agent 11 ~ 15, 11 ~ 15 auxiliary foaming agent; high temperature resistance provided by the embodiment of the invention of silicone containing arylacetylene resin foam material. Compared with the prior art, is the positive effect of the invention, the invention provides a silicone containing arylacetylene resin itself can be used as high temperature resistance, erosion resistance, high temperature resistant ceramic precursor; foaming after both of these special properties but also has the thermal insulation foam products, low density etc. in the field of aerospace materials;, as a new type of resin foam material, has a more significant resistance to high temperature resistant performance.
【技术实现步骤摘要】
一种耐高温含硅氧烷芳炔树脂泡沫材料
本专利技术涉及树脂泡沫材料
，特别是涉及一种耐高温含硅氧烷芳炔树脂泡沫材料。
技术介绍
现有的有机高分子耐高温泡沫材料如聚氨酯泡沫、酚醛泡沫、环氧泡沫等使用温度一般较低，通常小于300℃，而一些无机类多孔性材料制备工艺复杂，对一些复杂构件难以成型，限制了其使用范围。含硅氧烷芳炔树脂是近年发展起来的有机无机杂化材料，该树脂具有优异的耐热性，优良的介电性能及高温陶瓷化性能，可作为耐高温烧蚀防热材料、耐高温透波材料以及耐高温陶瓷的前体，在航空航天领域具有广阔的应用前景。而含硅氧烷芳炔树脂泡沫材料重量轻，刚性大，尺寸稳定性好，耐化学腐蚀，耐热性好，使用温度可达500℃以上，可作为航天航空等领域理想的隔热材料。除此之外，采用本专利技术制备含硅氧烷芳炔树脂泡沫工艺简单，制得的泡沫材料泡孔均匀，吸水率小，压缩强度大，介电性能优异。
技术实现思路
本专利技术实施例的目的在于提供一种耐高温含硅氧烷芳炔树脂泡沫材料，以克服现有技术的不足。为达到上述目的，本专利技术实施例公开了一种耐高温含硅氧烷芳炔树脂泡沫材料，其特征在于，材料组份为：含硅氧烷芳炔...
【技术保护点】
一种耐高温含硅氧烷芳炔树脂泡沫材料，其特征在于：材料组份为：含硅氧烷芳炔树脂110份，发泡剂11～15份，助发泡剂11～15份。
【技术特征摘要】
1.一种耐高温含硅氧烷芳炔树脂泡沫材料，其特征在于：材料组份为：含硅氧烷芳炔树脂110份，发泡剂11～15份，助发泡剂11～15份。2.根据权利要求1所述的一种耐高温含硅氧烷芳炔树脂泡沫材料，其特征在于：所述的发泡剂为：偶氮二异丁腈、偶氮二甲酸二异丙酯、偶氮二甲酸二乙酯、二偶氮氨基苯、偶氮二甲酸钡、亚肼基二甲酰胺、甲苯磺酰肼(TSH)、二硝基五亚甲基四胺(DPT)、二甲基二亚硝基对苯二甲酰胺(NTA)、5-苯基四唑(5-PT)、苯磺酰肼(BSH)、对苯磺酰肼、二磺酰肼二苯砜、二苯二磺酰肼、苯二磺酰肼、对甲苯磺酰基氨基脲(PTSS)或联二脲。3.根据权利要求1所述的...
【专利技术属性】
技术研发人员：何珩，张宇军，
申请(专利权)人：安徽键合科技有限公司，
类型：发明
国别省市：安徽,34