一种降低复合材料微波固化应力的方法技术

一种降低复合材料微波固化应力的方法，其特征在于：在复合材料的微波固化过程中，树脂到达凝胶点后再进行一段固化温度随时间升高与降低，并循环变化直至复合材料完全固化的周期变化。本发明专利技术能降低复合材料微波固化过程中产生的应力，提高固化质量，为微波固化复合材料提供了理想的控温方法，为微波固化替代传统的热压罐固化奠定了基础，本发明专利技术能降低固化应力80%以上，能满足大型结构件的使用需要。

Method for reducing microwave curing stress of composite material

A method of reducing composite microwave curing stress, which is characterized in that the microwave curing process of composite material, resin to gel point after a curing temperature and decreased with time, and changes in circulation until fully cured composite cycle. The invention can reduce the stress caused by microwave curing process of composite materials, improve the curing quality, provides the ideal temperature control method for microwave curing of composite materials, laid the foundation for the microwave curing autoclave instead of the traditional, the invention can reduce the curing stress of more than 80%, can be used to meet the needs of large structures.

【技术实现步骤摘要】
一种降低复合材料微波固化应力的方法
本专利技术涉及一种复合材料成型技术，尤其是一种复合材料微波固化技术，具体地说是一种降低复合材料微波固化应力的方法。
技术介绍
众所周知，先进复合材料具有比强度和比模量高、抗疲劳性能好、耐腐蚀性能好和整体成型性好等许多优异特性，飞机上大量应用复合材料不仅可以明显地减轻飞机的结构重量，提高飞机的性能，还可以大大减少零部件数量，简化工装、利于进行大部件组装，加快制造周期。应用部位由次承力结构向主承力结构过渡，目前复合材料已广泛用于各种操纵面、机翼和机身等主承力部位。复材在复杂曲面构件上的应用越来越多，如进气道、机身段、压力隔框等。构件向整体成型、共固化方向发展，可以明显减少零件、紧固件和模具的数量，大幅度地减少装配工序，是复合材料结构减重的重要措施，也是降低成本的一种有效方法。目前，先进复合材料的主要成型工艺是热压罐固化工艺。将复合材料与成型模具封装后送入热压罐中，加温加压固化成型。热压罐固化工艺以热传导方式加热复合材料，复合材料内部的温差大；罐体内所有材料包括气体介质均需加热至高温，能耗高，固化周期长、效率低。微波固化复合材料工艺是一种极有潜力替代热压本文档来自技高网...

【技术保护点】
一种降低复合材料微波固化应力的方法，其特征在于：在复合材料的微波固化过程中，材料的加热温度随加热过程循环升高与降低，直至复合材料完全固化。

【技术特征摘要】
1.一种降低复合材料微波固化应力的方法，其特征在于：在复合材料的微波固化过程中，材料的加热温度随加热过程循环升高与降低，直至复合材料完全固化。2.根据权利要求1所述的方法，其特征在于：复合材料固化温度循环升高与降低的过程中，升降温变化幅度不小于10摄氏度，温度循环变化过程中的升温...

【专利技术属性】
技术研发人员：李迎光，李楠垭，周靖，
申请(专利权)人：南京航空航天大学，
类型：发明
国别省市：江苏,32