The invention relates to the field of wear-resistant POM material, and discloses a wear-resistant polyoxymethylene composition, a wear-resistant polyoxymethylene material and an application thereof. The wear polyoxymethylene composition comprises 55 to 95 parts by weight of POM, 0 to 25 parts by weight of polyolefin, 0.5 to 20 parts by weight of a polyamide, 0.5 to 20 parts by weight of filler, 0.1 to 2 parts by weight of a nucleating agent and 0.1 to 2 parts by weight of antioxidants. The wear-resistant polyoxymethylene composition is no longer containing polytetrafluoroethylene, has low mortar wear rate and friction coefficient, and has a high peeling strength between the metal and the metal.
【技术实现步骤摘要】
一种耐磨聚甲醛组合物、耐磨聚甲醛材料和应用
本专利技术涉及耐磨聚甲醛材料领域，具体涉及与金属复合具备粘结性的耐磨聚甲醛材料领域。特别地，涉及一种耐磨聚甲醛组合物、耐磨聚甲醛材料和应用。
技术介绍
目前，耐磨聚甲醛主要集中应用于制作具有高强度高耐磨要求的齿轮、轴承、机电设备、电动工具，仪表外壳等领域。对于耐磨聚甲醛改性的方法，目前现有技术主要是通过向POM体系中添加聚氨酯(TPU)和聚四氟乙烯(PTFE)来提高聚甲醛材料的韧性和耐磨性能，其制备方法也为行业内所熟知，即通过螺杆挤出机方式将混合后配料通过熔融、挤出、造粒来制备耐磨改性聚甲醛。CN101759957B公开了一种增强高耐磨聚甲醛组合物，其原料重量配比为：聚甲醛(POM)40～70％、聚氨酯(TPU)5～20％、玻璃纤维10～30％、聚四氟乙烯(PTFE)3～10％、抗氧剂0.1～0.5％，润滑剂0.1～0.5％；聚甲醛为均聚聚甲醛熔点为175℃，玻璃纤维为长玻无碱玻纤，聚四氟乙烯为粉状，抗氧剂为受阻酚类抗氧剂1076，润滑剂为TAF。CN101885896B公开了一种高韧性高耐磨聚甲醛复合物，各组分质量百分...
【技术保护点】
一种耐磨聚甲醛组合物，其特征在于，该耐磨聚甲醛组合物包括：55～95重量份的聚甲醛、0～25重量份的聚烯烃、0.5～20重量份的聚酰胺、0.5～20重量份的填料、0.1～2重量份的成核剂和0.1～2重量份的抗氧剂。
【技术特征摘要】
1.一种耐磨聚甲醛组合物，其特征在于，该耐磨聚甲醛组合物包括：55～95重量份的聚甲醛、0～25重量份的聚烯烃、0.5～20重量份的聚酰胺、0.5～20重量份的填料、0.1～2重量份的成核剂和0.1～2重量份的抗氧剂。2.根据权利要求1所述的耐磨聚甲醛组合物，其中，该耐磨聚甲醛组合物包括：70～90重量份的聚甲醛、5～20重量份的聚烯烃、0.5～10重量份的聚酰胺、0.5～10重量份的填料、0.1～1重量份的成核剂和0.1～1重量份的抗氧剂。3.根据权利要求1或2所述的耐磨聚甲醛组合物，其中，所述聚甲醛为均聚聚甲醛和/或共聚聚甲醛；所述聚甲醛的重均分子量为30,000～180,000。4.根据权利要求1或2所述的耐磨聚甲醛组合物，其中，所述聚烯烃选自聚乙烯、聚乙烯接枝共聚物、聚丙烯、聚丙烯接枝共聚物、三元乙丙橡胶、乙烯基弹性体、乙烯基弹性体接枝共聚物、丙烯基弹性体和丙烯基弹性体接枝共聚物物中的至少一种；所述聚烯烃的重均分子量为20,000～150,000。5.根据权利要求1或2所述的耐磨聚甲醛组合物，其中，所述聚酰胺选自PA6、PA66、PA11、PA12、PA46、PA610、PA612和PA1010中的至少一种；所述聚...
【专利技术属性】
技术研发人员：常贺飞，梁文斌，马伊，张寅灵，
申请(专利权)人：神华集团有限责任公司，北京低碳清洁能源研究所，
类型：发明
国别省市：北京,11