The invention discloses a building wall refractory material and a preparation method thereof, by weight, which comprises the following components: cement prepared 6 10 copies, 6 copies, 3 lime silica powder 1 4, fly ash 3 8 copies, 6 copies, 2 cellulose ether hydrophobic agent 1 4 copies, 5 copies of short cut fiber 1, water 18 35 copies, the preparation method is as follows: according to the weight, cement, lime, fly ash, silica powder added to the mixer, mixing 6 8 minutes, get the mixture, then add to the mixture cellulose ether, water repellent, short fiber, mixing 4 8 minutes after adding water, stirring can be used again after 35 minutes 15. The present invention has the advantages of good toughness and excellent fire resistance.
【技术实现步骤摘要】
一种建筑墙体耐火材料及其制备方法
本专利技术涉及建筑保温材料领域，具体来说是一种建筑墙体耐火材料及其制备方法。
技术介绍
建筑材料可分为结构材料、装饰材料和某些专用材料，结构材料包括木材、竹材、石材、水泥、混凝土、金属、砖瓦、陶瓷、玻璃、工程塑料、复合材料等，装饰材料包括各种涂料、油漆、镀层、贴面、各色瓷砖、具有特殊效果的玻璃等；专用材料指用于防水、防潮、防腐、防火、阻燃、隔音、隔热、保温、密封等。随着社会的不断进步和发展，我国的科技实力也不断增强，其中，建筑材料的保温性能等逐渐得到了改善，但是现有的建筑材料依然存在任性差，耐火性能不高的缺陷，一旦发生火灾，后果不堪设想，研究出一款韧性好、耐火性能高的去昂提材料，已成为当前的重要课题之一。
技术实现思路
本专利技术的目的是为了解决现有技术中的建筑材料存在任性差、耐火性能不好的缺陷，提供一种建筑墙体耐火材料及其制备方法来解决上述问题。为了实现上述目的，本专利技术的技术方案如下：本专利技术公开了一种建筑墙体耐火材料，按重量份计，由以下组分制备而成：水泥6-10份、生石灰3-6份、硅胶粉1-4份、煤灰粉3-8份、纤维素醚2-...
【技术保护点】
一种建筑墙体耐火材料，其特征在于：按重量份计，由以下组分制备而成：水泥6‑10份、生石灰3‑6份、硅胶粉1‑4份、煤灰粉3‑8份、纤维素醚2‑6份、憎水剂1‑4份、短切纤维1‑5份、水18‑35份。
【技术特征摘要】
1.一种建筑墙体耐火材料，其特征在于：按重量份计，由以下组分制备而成：水泥6-10份、生石灰3-6份、硅胶粉1-4份、煤灰粉3-8份、纤维素醚2-6份、憎水剂1-4份、短切纤维1-5份、水18-35份。2.根据权利要求1所述的一种建筑墙体耐火材料，其特征在于：按重量份计，由以下组分制备而成：水泥7-9份、生石灰4-5份、硅胶粉2-3份、煤灰粉4-7份、纤维素醚3-5份、憎水剂2-3份、短切纤维2-4份、水19-32份。3.根据权利要求1所述的一种建筑墙体耐火材料，其特征在于：按重量份计，由以下组分制备而成：水泥8份、生石灰4份、硅胶粉3份、煤灰粉5份、纤维素醚4份、憎水剂2份、短切纤维3份、水25份。4.根据权利要求1所述的一种建筑墙体耐火材料，其特征在于：按重量份计，由以下组分制备而成：水泥6份、生石灰3份、硅胶粉4份、煤灰粉8份、纤维素醚2份、憎水剂4份、短切纤维1份、水35份。5.根据权利要求1所述的一种建筑墙体耐火材料，其特征在于：按重量份...