一种铈镁复合氧化物纳米棒材料的制备方法技术

本发明专利技术涉及一种铈镁复合氧化物纳米棒材料的制备方法。该发明专利技术将水热合成法与喷雾干燥法结合起来，使用普通设备，制备工艺简单，适合工业化生产。该方法所制备的铈镁复合氧化物纳米棒材料，形貌均一，尺寸可控，热稳定性高，经500℃焙烧仍能保持良好的棒状形貌。该材料应用前景广阔，不仅可应用于热催化、光催化以及电催化反应，还可用于生物医药、发光材料等领域。

Preparation method of cerium magnesium composite oxide nanorod material

The invention relates to a preparation method of cerium magnesium composite oxide nanorod material. The invention combines the hydrothermal synthesis and the spray drying method, uses the common equipment, and has simple preparation process and is suitable for industrial production. The cerium magnesium composite oxide nanorods prepared by this method have uniform morphology, controllable size and high thermal stability. They can still maintain good rod shape after calcination at 500 DEG C. The material has a wide application prospect. It can be used not only in thermal catalysis, photocatalysis and electrocatalysis, but also in the fields of biomedicine, luminescent materials and so on.

【技术实现步骤摘要】
一种铈镁复合氧化物纳米棒材料的制备方法
本专利技术涉及一种铈镁复合氧化物纳米棒材料的制备方法，属于纳米材料制备

技术介绍
由于CeO2具有较高的储氧性能，常作为催化活性组分、助剂、载体，用于汽车尾气净化、甲烷催化燃烧、低温水煤气变换、蒸汽重整等反应中(E.Aneggi,etal,J.Alloy.Compd.,2006,408:1096；H.Zhu,etal,J.Catal.,2005,233:41；C.Sun,etal,Eur.J.Inorg.Chem.,2009,2009:3883；M.B.Boucher,etal,Phys.Chem.Chem.Phys.,2011,13:2517；Q.Fu,etal,Catal.Lett.,2001,77:87；N.Divins,etal,Catal.Today,2015,253:99)。Li等人的研究表明，调变纳米粒子尺寸、形貌会改变反应物的吸附和活化状态，从而影响催化反应性能(Y.Li,etal,Chem.Soc.Rev.,2014,43:1543)。Chen等人的研究表明，CeO2基纳米材料的物理化学性质不仅依赖于其尺寸效应，其形本文档来自技高网...

【技术保护点】
一种铈镁复合氧化物纳米棒材料，其特征在于，由Mg元素掺杂并进入CeO

【技术特征摘要】
1.一种铈镁复合氧化物纳米棒材料，其特征在于，由Mg元素掺杂并进入CeO2晶格而制成，铈镁的摩尔比为0.8～0.99:0.2～0.01。2.根据权利要求1所述的铈镁复合氧化物纳米棒材料，其特征在于，采用水热合成-喷雾干燥法，得到纳米棒状材料，其制备工艺简单。其具体步骤为：根据用量比例，将硝酸镁的水溶液加入到可溶于水的铈盐水溶液中，在室温下，不断磁力搅拌，再加入过量的沉淀剂，得到混合物。将得到的混合物封装在密闭容器中，老化20h以上，得到反应产物。将反应产物过滤、洗涤，然后喷雾干燥，再焙烧，即得该纳米棒材料。3.根据权利要求2所述的铈镁复合氧化物纳米棒材料的制备方法，其特征在于，铈盐为硝酸铈或硝酸铈氨。...

【专利技术属性】
技术研发人员：陈永东，王洪，李淑军，张雨，柳具盆，唐林茂，杨草萍，严红林，罗雨菲，王萍萍，
申请(专利权)人：西南石油大学，
类型：发明
国别省市：四川,51