The invention discloses a heat conduction type polypropylene and its preparation method, the quality of 100% polypropylene resin as the base, conductive filler 0.5 ~ 30%; 2,6 di Ding Ji paracresol 0.03 ~ 0.3%; [3 pentaerythritol (3 ', 5' uncle Ding Ji '4 hydroxy propyl propionate ester)] 0.02 ~ 0.2%; Asia three phosphoric acid (2,4 di Ding Benji) ester 0.02 ~ 0.15%; 3 (3,5 di Ding Ji 4 hydroxyphenyl) propionate eighteen alkyl 0.04 ~ 0.3%; February Guangxi thio alcohol ester 0.02 ~ 0.2%. Polypropylene, conductive filler and other additives in advance after mixing, extruding and granulating in 170 under 240 DEG C. The prepared polypropylene heat conductive filler is chemically bonded with polypropylene long chain graphene, and when addition amount is 0.5 to 30%, the thermal conductivity of polypropylene is obviously improved, and the thermal conductivity coefficient is up to 8.60W/mK.
【技术实现步骤摘要】
一种导热型聚丙烯及其制备方法
本专利技术是关于一种导热型聚丙烯及其制备方法，特别涉及一种新型改性石墨烯导热填料制备导热型聚丙烯的方法。
技术介绍
聚丙烯是一种性能优异、无毒、价格低廉、易加工成型的半透明结晶聚合物，在日常生活及工业生产中得到了广泛应用。但是聚丙烯的导热性能与大多数聚合物相同，导热系数很小，导热效率较差，限制了聚丙烯在导热领域的应用。例如化工换热器是化工公司常用设备，换热部件通常为管材。聚丙烯由于耐酸碱腐蚀，是常用的换热器管材原料，但是聚丙烯换热管的导热性能较差，直接影响换热效率。为了获得导热性能良好的聚丙烯产品，在树脂基体中加入导热填料是经济、快捷的方法之一。石墨烯是新型的高性能碳材料，是目前发现的最薄、强度最大、导热导电性能最强的一种新型纳米材料，科学家甚至预言石墨烯将“彻底改变21世纪”。石墨烯作为导热填料添加到树脂基体中改善聚合物的导热性能已经有所尝试。存在的问题是石墨烯在树脂基体中分散困难，石墨烯薄片团聚在一起，不能发挥大比表面积的优势。并且石墨烯和树脂基材界面呈现相分离特征，导致复合材料的导热性能提高不理想。然而，化学键接聚丙烯长链的石墨...
【技术保护点】
一种导热型聚丙烯，其特征是组成及其质量分数如下：聚丙烯树脂质量100％为基准，导热填料0.5～30％；2,6‑二叔丁基对甲酚0.03～0.3％；季戊四醇[3‑(3’,5’二叔丁基‑4’‑羟丙基)丙酸]酯0.02～0.2％；亚磷酸三(2,4‑二叔丁苯基)酯0.02～0.15％；3‑(3,5‑二叔丁基‑4‑羟基苯基)丙酸十八烷基酯0.04～0.3％；硫代丙酸二月桂醇酯0.02～0.2％；导热填料为化学键接有聚丙烯长链的石墨烯，其结构如下所示：
【技术特征摘要】
1.一种导热型聚丙烯，其特征是组成及其质量分数如下：聚丙烯树脂质量100％为基准，导热填料0.5～30％；2,6-二叔丁基对甲酚0.03～0.3％；季戊四醇[3-(3’,5’二叔丁基-4’-羟丙基)丙酸]酯0.02～0.2％；亚磷酸三(2,4-二叔丁苯基)酯0.02～0.15％；3-(3,5-二叔丁基-4-羟基苯基)丙酸十八烷基酯0.04～0.3％；硫代丙酸二月桂醇酯0.02～0.2％；导热填料为化学键接有聚丙烯长链的石墨烯，其结构如下所示：其中：为石墨烯。2.权利要求1的导热型聚丙烯的制备方法，其特征是将聚丙烯、导热填料、2,6-二叔丁基对甲酚、季戊四醇[3-(3...