The invention provides a nitrile rubber hollow fiber damping materials prepared by the following method: 1) the nitrile rubber / organic modified bentonite composite and PVC mixing in the mixing machine, electric heating plate vulcanizing machine made of laminated sheet to sheet and method; 2) the lubricant prepared by the mixer mixing, after curing the plunger extruder paste extrusion of nitrile rubber hollow fiber, the nitrile rubber hollow fiber extrusion of degreasing and removing the lubricant, and then drawing and sintering, made of nitrile rubber hollow fiber. The acrylonitrile butadiene rubber hollow fiber structure damping material has good damping performance.
【技术实现步骤摘要】
丁腈橡胶中空纤维结构阻尼材料
本专利技术涉及丁腈橡胶中空纤维结构阻尼材料，属于阻尼材料
技术介绍
中空纤维是指纤维轴向有细管状空腔的化纤。贯通纤维轴向具有管状空腔的化学纤维。可用于冬装、被褥和衬垫用絮片等；组装成微滤、超滤、透析、气体分离、反渗透及蒸发渗透器等。中空纤维结构，包含大量静止空气，能为织物带来轻质弹性、良好透湿性以及舒适的保暖效果，广泛用于保暖内衣、贴身内衣、运动服装、休闲服装、衬衫、户外运动以及毯子等多个领域。中空纤维，按其作用分两类：①絮片用，中空度要求不高，约30%～100%，主要追求轻而保暖，为了提高其回弹率，还可制成偏芯中空纤维，经热处理而形成三维卷曲；②分离膜用，中空度和截面圆整度要求高，膜壁微孔及其分布有一定要求，还可涂一层或两层不同超薄分离层，以提高分离效果和选择性。目前丁腈橡胶中空纤维结构用于阻尼材料的报道还比较少。
技术实现思路
本专利技术的目的是克服现有技术的不足，提供一种丁腈橡胶中空纤维结构阻尼材料。本专利技术的丁腈橡胶中空纤维结构阻尼材料，通过如下方法制备而成：1）将丁腈橡胶/有机改性膨润土复合材料与PVC在开炼机上混炼，用电热平板硫化机以层压法制成片材；2）将制成的片材与润滑剂采用混合器进行混合，熟化后采用柱塞挤出机糊料挤出丁腈橡胶中空纤维，将挤出的丁腈橡胶中空纤维进行脱脂和脱除润滑剂，然后进行牵伸和烧结，制得丁腈橡胶中空纤维。所述的步骤1）中，层压法过程如下：温度为180±5℃,以4MPa的压力预热4min,以15MPa的压力热压3min,在15MPa的压力下冷压至常温出模。本专利技术的丁腈橡胶中空纤维结构阻...
【技术保护点】
丁腈橡胶中空纤维结构阻尼材料，其特征在于，通过如下方法制备而成：1）将丁腈橡胶/有机改性膨润土复合材料与 PVC 在开炼机上混炼，用电热平板硫化机以层压法制成片材；2）将制成的片材与润滑剂采用混合器进行混合， 熟化后采用柱塞挤出机糊料挤出丁腈橡胶中空纤维，将挤出的丁腈橡胶中空纤维进行脱脂和脱除润滑剂，然后进行牵伸和烧结，制得丁腈橡胶中空纤维。
【技术特征摘要】
1.丁腈橡胶中空纤维结构阻尼材料，其特征在于，通过如下方法制备而成：1）将丁腈橡胶/有机改性膨润土复合材料与PVC在开炼机上混炼，用电热平板硫化机以层压法制成片材；2）将制成的片材与润滑剂采用混合器进行混合，熟化后采用柱塞挤出机糊料挤出丁腈橡胶中空纤维，将挤出的丁腈橡胶中空纤维进...